Can coatings

1. A coated substrate comprising:

a substrate,

a base coating resin with micro-impressions and planar areas, and

an overlay coating resin;

wherein the coated substrate adheres to the formula:

P*T B > A*T O ;

wherein:

T B , is a tensile strength of the base coating resin;

T O is a tensile strength of the overlay coating resin;

A is the area of the micro-impressions; and

P is the area of the planar areas.

2. The coated substrate of claim 1 , wherein T B is greater than T O .

3. The coated substrate of claim 1 , wherein the base coating resin comprises an epoxy resin.

4. The coated substrate of claim 3 , wherein the epoxy resin comprises bis-phenol A epoxy resin.

5. The coated substrate of claim 1 , wherein the overlay coating resin is a polypropylene resin, a polyethylene resin, a polyethylene terephthalate resin, a polyurethane resin, or a blend of any two or more resins thereof, or a copolymer of any two or more such resins.

6. The coated substrate of claim 5 , wherein the overlay coating resin is a polyethylene terephthalate resin, or a blend thereof.

7. The coated substrate of claim 1 , wherein the micro-impressions are filled with the overlay coating resin.

8. The coated substrate of claim 1 , wherein the area of the micro-impressions is from about 0.001 μM 2 to about 1000 μM 2 .

9. The coated substrate of claim 1 , wherein T B is from about 50 MPa to about 100 MPa, from about 55 MPa to about 90 MPa, from about 60 MPa to about 85 MPa, from about 65 MPa to about 80 MPa, or from about 65 MPa to about 75 MPa.

10. The coated substrate of claim 9 , wherein T B is from about 65 MPa to about 75 MPa.

11. The coated substrate of claim 1 , wherein T O is from about 70 MPa to about 110 MPa, from about 75 MPa to about 105 MPa, from about 75 MPa to about 100 MPa, from about 80 MPa to about 95 MPa, or from about 80 MPa to about 90 MPa.

12. The coated substrate of claim 11 , wherein T O is from about 80 MPa to about 90 MPa.

13. A process of preparing a coated substrate comprising:

applying a base coating to a substrate;

micro-impressioning a top surface of the base coating resin to provide a micro-impressioned top surface of the base coating comprising micro-impressions and non-impressioned planar areas; and

applying an overlay coating resin to the micro-impressioned top surface of the base coating;

wherein the coated substrate adheres to the formula:

P*T B > A*T O ; wherein:

A is the area of the micro-impressions;

P is the area of the non-impressioned planar areas;

T B is a tensile strength of the base coating resin; and

T O is a tensile strength of the overlay coating resin.

14. The process of claim 13 further comprising contacting the micro-impressioned top surface of the base coating with a solvent prior to applying the overlay coating resin, to extract unreacted or excess materials of the base coating.

15. The process of claim 14 , wherein the unreacted or excess materials comprise bis-phenol A epoxy resin.

16. The process of claim 13 further comprising curing the base coating resin to form a cured based coating resin, wherein the micro-impressioning comprises boring holes into the top surface of the cured base coating resin.

17. The process of claim 13 , wherein the micro-impressioning comprises rolling or stamping micro-impressions into the top surface of the base coating resin.

18. The process of claim 13 further comprising curing the base coating resin to form a cured based coating resin, and the micro-impressioning comprises applying a stamp comprising micro-protrusions to the cured or curing base coating resin.

19. The process of claim 13 , wherein the substrate is a metal blank for the formation of a can.

20. The coated substrate of claim 1 , wherein the substrate comprises a can.