Pelletization of pyrolyzed rubber products
A system and method for preparing a pelletized carbon black product is provided. The system includes a source of a carbon black product from a pyrolysis process. A mixer is in communication with the source of the carbon black product. A binder oil storage tank is in fluid communication with the mixer. The binder oil storage tank is configured to inject a desired amount of a binder oil into the mixer to form the pelletized carbon black product.
1. A pelletized tire pyrolysis product, comprising:
a carbon black product in an amount greater than about 85 percent by weight relative to the total weight of the pelletized tire pyrolysis product, the carbon black product formed from a carbonaceous char derived from pyrolysis of at least one of whole tires and tire shreds, the whole tires and the tire shreds having steel belt wire and zinc from zinc oxide present in tire rubber compounds, the carbon black product further comprising:
a carbon black in an amount between 65 percent and 95 percent,
an organic volatile material in an amount between 5 percent and 15 percent in the form of residual polymer and hydrocarbons remaining at an end of the pyrolysis of the at least one of the whole tires and the tire shreds,
an inorganic ash in an amount in an amount up to 15 percent, wherein all percentages are by weight relative to the total weight of the carbon black product; and
a binder oil that agglomerates the carbon black product into substantially free-flowing pellets, wherein the binder oil is derived from the pyrolysis of the at least one of the whole tires and the tire shreds and has an iron content and a zinc content,
wherein individual pellets of the pelletized carbon black product have an average diameter from about 0.125 inches to about 0.0625 inches,
wherein an ASTM D3191 standard styrene butadiene rubber formulation with the carbon black product has a tensile strength between 2800 psi and 3500 psi, and
wherein the carbon black product is pulverized to about a 325 mesh particle size, with 99.99% of the pulverized carbon black product able to pass through a 325 mesh screen, prior to combining the carbon black product with the binder oil into the substantially free-flowing pellets.
2. The pelletized tire pyrolysis product according to claim 1 , wherein the carbon black is present in the carbon black product at 85 percent, the organic volatile material at 5 percent, and the inorganic ash at 10 percent, wherein all percentages are by weight relative to the total weight of the carbon black product.
3. The pelletized tire pyrolysis product according to claim 1 , wherein the carbon black product is substantially metal-free.
4. The pelletized tire pyrolysis product according to claim 1 , wherein the binder oil is present in an amount up to about 15 percent by weight relative to the total weight of the pelletized tire pyrolysis product.
5. The pelletized tire pyrolysis product according to claim 1 , wherein the carbon black is present in the carbon black product in an amount between about 85 percent and about 95 percent, and the inorganic ash is present in the carbon black product in an amount between about 9 percent and about 12 percent, wherein all percentages are by weight relative to the total weight of the carbon black product.
6. The pelletized tire pyrolysis product according to claim 1 , wherein the at least one of the whole tires and the tires shreds are pyrolyzed according to a time-temperature profile that does not exceed a temperature of 870° F.
7. The pelletized tire pyrolysis product according to claim 4 , wherein the desired amount of binder oil is about 12.5 percent by weight in relation to the total weight of the pelletized carbon black product.
8. The pelletized tire pyrolysis product according to claim 1 , wherein an average particle size of the pulverized carbon black product prior to pelletization is about five microns.
9. A pelletized tire pyrolysis product, comprising:
a carbon black product in an amount greater than about 85 percent by weight relative to the total weight of the pelletized tire pyrolysis product, the carbon black product formed from a carbonaceous char derived from pyrolysis of at least one of whole tires and tire shreds, the whole tires and the tire shreds having steel belt wire and zinc from zinc oxide present in tire rubber compounds, the carbon black product further comprising:
a carbon black in an amount between 65 percent and 95 percent,
an organic volatile material in an amount between 5 percent and 15 percent in the form of residual polymer and hydrocarbons remaining at an end of the pyrolysis of the at least one of the whole tires and the tire shreds,
an inorganic ash in an amount in an amount up to 15 percent, wherein all percentages are by weight relative to the total weight of the carbon black product; and
a binder oil that agglomerates the carbon black product into substantially free-flowing pellets, wherein the binder oil is derived from the pyrolysis of the at least one of the whole tires and the tire shreds and has an iron content and a zinc content,
wherein an ASTM D3191 standard styrene butadiene rubber formulation with the carbon black product has a tensile strength between 2800 psi and 3500 psi.