Mixed-layered bismuth-oxygen-iodine materials for capture and waste disposal of radioactive iodine
View Patent ↗Materials and methods of synthesizing mixed-layered bismuth oxy-iodine materials, which can be synthesized in the presence of aqueous radioactive iodine species found in caustic solutions (e.g. NaOH or KOH). This technology provides a one-step process for both iodine sequestration and storage from nuclear fuel cycles. It results in materials that will be durable for repository conditions much like those found in Waste Isolation Pilot Plant (WIPP) and estimated for Yucca Mountain (YMP). By controlled reactant concentrations, optimized compositions of these mixed-layered bismuth oxy-iodine inorganic materials are produced that have both a high iodine weight percentage and a low solubility in groundwater environments.
1. A mixed-layered bismuth oxy-iodine material, comprising a chemical assemblage at an atomistic scale of at least two different Bi—O—I lattice phases.
2. The material of claim 1 , wherein the at least two different Bi—O—I lattice phases comprise BiOI and Bi 5 0 7 I lattice phases.
3. The material of claim 2 , wherein the relative proportions of the BiOI and Bi 5 O 7 I lattice phases is 85-80 mole % BiOI and 15-20 mole % Bi 5 0 7 I.
4. The material of claim 1 , wherein the mixed-layered bismuth oxy-iodine material has an elemental composition comprising 17-22 wt % iodine, with the balance comprising primarily bismuth and oxygen.
5. The material of claim 1 , wherein the mixed-layered bismuth oxy-iodine material 20 has a bismuth-to-iodine (Bi:I) molar ratio of between 1.64 and 2.13.
6. The material of claim 1 , wherein the mixed-layered bismuth oxy-iodine material has a iodine solubility equal to or less than 15 ppb, after exposing the material for 3 days to deionized water at a temperature of 25° C. or lower.
7. The material of claim 1 , wherein the mixed-layered bismuth oxy-iodine material has a iodine solubility equal to or less than 100 ppb, after exposing the material for 3 days to deionized water at a temperature of 94° C. or lower.
8. The material of claim 1 , wherein the mixed-layered bismuth oxy-iodine material has a iodine solubility equal to or less than 100 ppm, after exposing the material for 3 days to deionized water plus 0.005 molar sodium sulfate at a temperature of 25° C. or lower.
9. The material of claim 1 , wherein the mixed-layered bismuth oxy-iodine material has a iodine solubility equal to or less than 1000 ppm, after exposing the material for 3 days to deionized water plus 0.005 molar bicarbonate at a temperature of 25° C. or lower.
10. The material of claim 1 , wherein the mixed-layered bismuth oxy-iodine material has a iodine solubility equal to or less than about 1 ppm, after exposing the material for 3 days to deionized water plus 0.005 molar chloride at a temperature of 25° C. or lower.
11. The material of claim 1 , wherein the iodine in the mixed-layered bismuth oxy-iodine material comprises radioactive 129 I.