Colloidal nanoparticle materials for photodetectors and photovoltaics
A composite material is described. The composite material comprises semiconductor nanocrystals, and organic molecules that passivate the surfaces of the semiconductor nanocrystals. One or more properties of the organic molecules facilitate the transfer of charge between the semiconductor nanocrystals. A semiconductor material is described that comprises p-type semiconductor material including semiconductor nanocrystals. At least one property of the semiconductor material results in a mobility of electrons in the semiconductor material being greater than or equal to a mobility of holes. A semiconductor material is described that comprises n-type semiconductor material including semiconductor nanocrystals. At least one property of the semiconductor material results in a mobility of holes in the semiconductor material being greater than or equal to a mobility of electrons.
1. A method of making ternary or quaternary chalcopyrite nanoparticles, the method including:
preparing a first solution and bringing it to a first temperature, the first solution including salts that include at least one metal selected from the group including copper (Cu), indium (In), and gallium (Ga);
preparing a second solution and bringing it to a second temperature, the second solution including selenium powder dissolved in oleylamine, the second temperature being in the range of about 200° C. to about 300° C.; and
injecting the second solution into the first solution.
2. The method of claim 1 , wherein the first solution includes a salt selected from the list including at least one of the following: Cu(acac) 2 , In(acac) 3 , and Ga(acac) 3 .
3. A method of making ternary or quaternary chalcopyrite nanoparticles, the method including:
preparing a first solution and bringing it to a first temperature, the first solution including a salt selected from the list including at least one of the following: Cu(acac) 2 , In(acac) 3 , and Ga(acac) 3 ;
preparing a second solution and bringing it to a second temperature, the second solution including selenium powder dissolved in oleylamine, the second temperature being in the range of about 200° C. to about 300° C.; and
injecting the second solution into the first solution.