Catalyst for treating exhaust gases, method for producing the same, and method for treating exhaust gases
A catalyst for treating exhaust gases containing nitrogen monoxide, carbon monoxide and volatile organic compounds includes a plurality of layers, an upper layer of which has an active component contained uniformly therein and a lower layer of which has no active component contained therein. The catalyst is obtained through the steps of: forming the lower layer by coating the surface of substrate with a slurry of a porous inorganic compound, followed by drying; and forming the upper layer, which is to be the top surface of the catalyst, by coating the surface of the lower layer with a slurry of a porous inorganic compound that has the active component composed of one or more precious metals supported thereon, followed by drying. The oxidation power of the resulting catalyst is enhanced without increasing the amount of precious metal supported thereon.
1. A method of treating exhaust gases containing nitrogen monoxide, carbon, and carbon compounds comprising:
preparing a catalyst by the steps of:
forming a lower coat layer having a thickness of 20 to 100 μm by coating the surface of a substrate with a slurry of a porous inorganic compound, followed by drying;
preparing a colloidal solution of one or more precious metals;
allowing the one or more precious metals to be supported on a porous inorganic compound by using the colloidal solution;
preparing a slurry of the porous inorganic compound having the one or more precious metals supported thereon; and
forming an upper coat layer having a thickness of 4 to 30 μm, which is to be the top surface of the catalyst, by coating the surface of the lower coat layer with the slurry, followed by drying,
wherein a population of particles that have a multi-peak particle size distribution is used as the porous inorganic compound; and
exposing the exhaust gases to a catalyst in a manner sufficient to catalyze reduction of the exhaust gases.
2. The method of treating exhaust gases according to claim 1 , wherein in the step of forming an upper coat layer, calcining is performed after the drying.
3. The method of treating exhaust gases according to claim 1 , wherein in the step of forming a lower coat layer, a slurry of a porous inorganic compound having one or more precious metals supported thereon is used as the slurry of a porous inorganic compound, and the amount of the precious metal(s) supported on the porous inorganic compound used in the step of forming a lower coat layer is smaller than that of the precious metal(s) supported on the porous inorganic compound used in the step of forming an upper coat layer.
4. The method of treating exhaust gases according to claim 1 , wherein in the step of forming a lower coat layer, a slurry of a porous inorganic compound having one or more precious metals supported thereon is used as the slurry of a porous inorganic compound and the amount of the precious metal(s) supported on the porous inorganic compound used in the step of forming a lower coat layer is 0.3 to 1.5 g/L, while the amount of the precious metal(s) supported on the porous inorganic compound used in the step of forming an upper coat layer is 0.3 to 1.5 g/L.
5. The method of treating exhaust gases according to claim 1 , wherein the step of preparing the colloidal solution comprises mixing an aqueous solution of a salt or salts of the one or more precious metals with water, a reducing agent and a polymer material; and
subjecting the mixture to a reduction treatment to form colloidal particles of the precious metal.
6. The method of treating exhaust gases according to claim 5 , wherein the reducing agent comprises an organic acid.
7. The method of treating exhaust gases according to claim 6 , wherein the polymer material comprises a water-soluble polymer.
8. The method of treating exhaust gases according to claim 1 , wherein the step of allowing the precious metal to be supported on the porous inorganic compound comprises spray drying, vaporization to dryness, or adsorption of the colloidal solution.
9. A method of treating exhaust gases containing nitrogen monoxide, carbon, and carbon compounds comprising:
preparing a catalyst by the steps of:
forming a lower coat layer having a thickness of 20 to 100 μm by coating the surface of a substrate with a slurry of a porous inorganic compound, followed by drying;
preparing a colloidal solution of one or more precious metals;
allowing the one or more precious metals to be supported on a porous inorganic compound by using the colloidal solution;
preparing a slurry of the porous inorganic compound having the one or more precious metals supported thereon; and
forming an upper coat layer having a thickness of 4 to 30 μm, which is to be the top surface of the catalyst, by coating the surface of the lower coat layer with the slurry, followed by drying,
wherein in the step of forming a lower coat layer, a slurry of a porous inorganic compound having one or more precious metals supported thereon is used as the slurry of a porous inorganic compound, and the amount of the precious metal(s) supported on the porous inorganic compound used in the step of forming a lower coat layer is smaller than that of the precious metal(s) supported on the porous inorganic compound used in the step of forming an upper coat layer; and
exposing the exhaust gases to a catalyst in a manner sufficient to catalyze reduction of the exhaust gases.
10. The method of treating exhaust gases according to claim 9 , wherein a population of particles that have a multi-peak particle size distribution is used as the porous inorganic compound.
11. The method of treating exhaust gases according to claim 9 , wherein in the step of forming an upper coat layer, calcining is performed after the drying.
12. The method of treating exhaust gases according to claim 9 , wherein in the step of forming a lower coat layer, a slurry of a porous inorganic compound having one or more precious metals supported thereon is used as the slurry of a porous inorganic compound and the amount of the precious metal(s) supported on the porous inorganic compound used in the step of forming a lower coat layer is 0.3 to 1.5 g/L, while the amount of the precious metal(s) supported on the porous inorganic compound used in the step of forming an upper coat layer is 0.3 to 1.5 g/L.
13. The method of treating exhaust gases according to claim 9 , wherein the step of preparing the colloidal solution comprises
mixing an aqueous solution of a salt or salts of the one or more precious metals with water, a reducing agent and a polymer material; and
subjecting the mixture to a reduction treatment to form colloidal particles of the precious metal.
14. The method of treating exhaust gases according to claim 13 , wherein the reducing agent comprises an organic acid.
15. The method of treating exhaust gases according to claim 14 , wherein the polymer material comprises a water-soluble polymer.
16. The method of treating exhaust gases according to claim 9 , wherein the step of allowing the precious metal to be supported on the porous inorganic compound comprises spray drying, vaporization to dryness, or adsorption of the colloidal solution.