Preparation of supported electrocatalyst comprising multiwalled carbon nanotubes
View Patent ↗A process for preparing a durable non-precious metal oxygen reduction electrocatalyst involves heat treatment of a ball-milled mixture of polyaniline and multiwalled carbon nanotubes in the presence of a Fe species. The catalyst is more durable than catalysts that use carbon black supports. Performance degradation was minimal or absent after 500 hours of operation at constant cell voltage of 0.40 V.
1. A process for preparing a supported electrocatalyst, comprising:
treating a sample of multiwalled carbon nanotubes with an aqueous hydrochloric acid solution to remove impurities from the carbon nanotubes, and thereafter
treating the multiwalled carbon nanotubes with a solution comprising nitric acid and sulfuric acid, thereby providing oxidized multiwalled carbon nanotubes,
mixing the oxidized multiwalled carbon nanotubes with a mixture comprising polyaniline and a Fe species, and thereafter
vacuum-drying the mixture comprising multiwalled carbon nanotubes, polyaniline, and a Fe species to form a vacuum-dried mixture, and thereafter
subjecting the vacuum-dried mixture to ball-milling for 24 hours, and thereafter
heating the ball-milled mixture at a first temperature in an inert atmosphere, and thereafter
cooling the ball milled mixture, and thereafter
treating the cooled, ball milled mixture with aqueous sulfuric acid, and thereafter,
heat-treating the mixture at a second temperature in an inert atmosphere, thereby forming the supported electrocatalyst.
2. The process of claim 1 , wherein the multiwalled carbon nanotubes have a BET surface area of approximately 230 square meters per gram.
3. The process of claim 1 , wherein the aqueous hydrochloric acid solution comprises 1.0 molar hydrochloric acid.
4. The process of claim 1 , wherein the step of mixing the oxidized multiwalled carbon nanotubes with a mixture comprising polyaniline and a Fe species comprises:
dispersing aniline in hydrochloric acid and thereafter adding the oxidant ammonium persulfate and ferric chloride, thereby forming a mixture comprising polyaniline and a Fe species, and thereafter,
mixing oxidized multiwalled carbon nanotubes with the mixture comprising polyaniline and a Fe species.
5. The process of claim 1 , wherein the first temperature is approximately 900° C.
6. The process of claim 1 , wherein the second temperature is approximately 900° C.