Composite for anode material, anode materials and lithium battery using the same
Provided is a composite for anode material, a method of manufacturing the composite for anode material, and a cathode and a lithium battery that includes the composite for anode material, and more particularly, to a composite for anode material that has a large charge and discharge capacity and a high capacity retention, a method of manufacturing the composite for anode material, and a cathode and a lithium battery that includes the composite for anode material. Also, the composite for anode material in which Si or Si and carbon are distributed in silicon oxide particles is provided.
1. A composite for an anode material comprising Si particles and carbon coated with silicon oxide particles, and carbon on external surfaces of the silicon oxide particles, wherein a content of Si particles in the silicon oxide particles is 10 to 20 parts by weight based on 100 parts by weight of silicon oxide, and a content of carbon in the silicon oxide particles is 20 to 40 parts by weight based on 100 parts by weight of silicon oxide.
2. The composite of claim 1 , wherein a molar ratio of oxygen to silicon in the silicon oxide particles is 0.5 to 1.95.
3. The composite of claim 1 , wherein the Si particles have an average particle diameter of 0.01 to 5 μm.
4. The composite of claim 1 , wherein the carbon is a crystalline state carbon or an amorphous state carbon.
5. An anode material comprising the composite according to claim 1 .
6. The anode material of claim 5 , wherein a molar ratio of oxygen to silicon in the silicon oxide particles is 0.5 to 1.95.
7. The anode material of claim 5 , wherein the anode material further comprises carbon.
8. The anode material of claim 5 , wherein the anode material further comprises a material that is able to form an alloy with lithium.
9. The anode material of claim 8 , wherein the material that is able to form an alloy with lithium is at least one selected from the group consisting of Si, SiO x (0.8<x≦2), Sn, SnO x (0<x≦2), Ge, GeO x (0<x≦2), Pb, PbO x (0<x≦2), Ag, Mg, Zn, ZnO x (0<x≦1), Ga, In, Sb, and Bi.
10. A lithium battery comprising:
an anode comprising a metal current collector and the anode material of claim 5 coated on the metal current collector;
a cathode; and
an electrolyte.
11. A lithium battery of claim 10 , wherein a molar ratio of oxygen to silicon in the silicon oxide particles is 0.5 to 1.95.
12. The composite of claim 1 , where a mixing ratio of silicon oxide:Si:carbon is 1:0.1:0.2 or 0.5:0.1:0.2 by weight.