Methods for improving multimodal polyethylene and films produced therefrom
A blown film composition including a first high density polyethylene component and a second high density polyethylene component, wherein the blown film contains a mixture of three or more discrete molecular weight distributions, and wherein the second high density polyethylene component has at least one more discrete molecular weight distribution than the first high density polyethylene component.
1. A blown film composition comprising:
a first high density polyethylene component;
a second high density polyethylene component that is bimodal; and
a polyethylene compatible nucleating agent.
2. The composition of claim 1 , wherein the blown film composition has three or more discrete molecular weight distributions.
3. The composition of claim 1 , wherein the blown film composition has improved barrier properties over a comparable composition without the nucleating agent.
4. The composition of claim 3 , wherein the blown film composition has improved bubble stability over a comparable composition without the nucleating agent.
5. The composition of claim 3 , wherein the blown film composition has improved dart impact resistance over a comparable composition without the nucleating agent.
6. The composition of claim 1 , wherein the first high density polyethylene component has a density ranging from 0.950 to 0.970 g/cm 3 .
7. The composition of claim 1 , wherein the first high density polyethylene component is unimodal.
8. The composition of claim 1 , wherein the second high density polyethylene component comprises a density ranging from 0.945 to 0.970 g/cm 3 .
9. The composition of claim 1 , wherein the first high density polyethylene component is present in amounts ranging from 60 to 99 wt % based on the total weight of the blown film composition.
10. The composition of claim 1 , wherein at max frost line height, the blown film composition comprises a WVTR of less than 0.250 g /100 in 2 /day.
11. The composition of claim 1 , wherein the blown film composition has a WVTR that is less than the WVTR of either the first or second high density polyethylene component absent the polyethylene compatible nucleating agent.
12. The composition of claim 1 , wherein blown film composition has a decrease in haze of at least 10% and an increase in gloss of at least 10% over an identical blown film composition absent the polyethylene compatible nucleating agent.
13. The composition of claim 1 , wherein blown film composition has a decrease in haze of at least 20% and an increase in gloss of at least 40% at max frost line height over an identical blown film composition absent the polyethylene compatible nucleating agent.
14. The composition of claim 1 , wherein the weight ratio of the first high density polyethylene component to the second high density polyethylene component ranges from 25:1 to 3:1.
15. An article made from a blown film composition comprising:
a first high density polyethylene component;
a second high density polyethylene component that is bimodal; and
a polyethylene compatible nucleating agent.
16. A multimodal blend comprising:
a first high density polyethylene component;
a second high density polyethylene component that is bimodal; and
a polyethylene compatible nucleating agent;
wherein the multimodal blend is a mixture of three or more discrete molecular weight distributions;
wherein the weight ratio of the first high density polyethylene component to the second high density polyethylene component in the multimodal blend is from 25:1 to 3:1;
wherein at max frost line height, the multimodal blend has a WVTR of less than 0.250 g/100 in 2 /day.
17. The blend of claim 16 , wherein the first high density polyethylene component is unimodal.
18. The blend of claim 16 , wherein the blend has a decrease in haze of at least 10% and an increase in gloss of at least 10% over an identical blend absent the polyethylene compatible nucleating agent.
19. An article made from a multimodal blend comprising:
a first high density polyethylene component;
a second high density polyethylene component that is bimodal; and
a polyethylene compatible nucleating agent;
wherein the multimodal blend is a mixture of three or more discrete molecular weight distributions;
wherein the weight ratio of the first high density polyethylene component to the second high density polyethylene component in the multimodal blend is from 25:1 to 3:1;
wherein at max frost line height, the multimodal blend has a WVTR of less than 0.250 g/100 in 2 /day.
20. A method of making a multimodal film comprising:
combining a first high density polyethylene component, a second high density polyethylene component that is bimodal, and a polyethylene compatible nucleating agent, to form a multimodal resin having three or more discrete molecular weight distributions;
wherein the second high density polyethylene component has at least one more discrete molecular weight distribution than the first high density polyethylene component.
21. The method of claim 20 , wherein the multimodal film is a blown film.
22. The method of claim 20 , wherein the weight ratio of the first high density polyethylene component to the second high density polyethylene component in the multimodal resin is from 25:1 to 3:1, and wherein at max frost line height, the multimodal resin has a WVTR of less than 0.250 g/100 in 2 /day.