Rubber composition for bead apex and tire having bead apex prepared using same
There is provided a rubber composition for a bead apex which can enhance extrusion processability by optimizing a rate of vulcanization during a vulcanization process, and can improve rigidity, steering stability and a low fuel consumption property, a tire having a bead apex prepared by using the rubber composition for a bead apex and being capable of enhancing steering stability and reducing rolling resistance and a tire for a sports utility vehicle (SUV) having further enhanced durability. The rubber composition for a bead apex comprises a diene rubber, a phenol resin and/or a modified phenol resin, sulfur, hexamethylenetetramine, a vulcanization accelerator, and at least one kind of vulcanization acceleration auxiliary selected from the group consisting of a citraconimide compound, a condensate of alkyl phenol and sulfur chloride, an organic thiosulfate compound and a compound represented by the general formula: R 1 —S—S-A-S—S—R 2 .
1. A bead apex composed of a rubber composition for a bead apex, said rubber composition comprising:
5 to 25 parts by weight of a phenol resin and/or a modified phenol resin;
5.25 to 6.5 parts by weight of sulfur;
1.0 to 2.5 parts by weight of hexamethylenetetramine;
2.0 to 5.0 parts by weight of a benzothiazole vulcanization accelerator which may contain a sulfenamide moiety; and
0.1 to 5 parts by weight of a condensate of alkyl phenol and sulfur chloride represented by the following chemical formula:
wherein n is 0 or an integer of 1 to 10, X is an integer of 2 to 4, and R is an alkyl group having 8 carbon atoms, and
100 parts by weight of a diene rubber that is at least one member selected from the group consisting of natural rubbers, isoprene rubbers, butadiene rubbers, styrene-butadiene rubbers, and mixtures thereof,
wherein the rubber composition has a Mooney scorch time of not less than 7.0 minutes and not more than 30 minutes.
2. The bead apex of claim 1 , wherein the total amount of hexamethylenetetramine and benzothiazole vulcanization accelerator which may contain a sulfenamide moiety is 3.5 to 7.5 parts by weight based on 100 parts by weight of the diene rubber.
3. The bead apex of claim 1 , wherein said diene rubber is a natural rubber.
4. The bead apex of claim 1 , wherein the amount of condensate of alkyl phenol and sulfur chloride is 0.5 to 3.0 parts by weight based on 100 parts by weight of the diene rubber.
5. A tire having the bead apex of claim 1 .
6. A tire for a sports utility vehicle having the bead apex of claim 1 .
7. A tire having the bead apex of claim 2 .
8. A tire having the bead apex of claim 3 .
9. A tire having the bead apex of claim 4 .