Solar heat-reflective roofing granules, solar heat-reflective shingles, and process for producing the same
A process for preparing roofing granules includes forming kaolin clay into green granules and sintering the green granules at a temperature of at least 900 degrees Celsius to cure the green granules until the crystalline content of the sintered granules is at least ten percent as determined by x-ray diffraction.
1. A process for forming bituminous roofing products with high solar heat reflectance, the process comprising:
(a) providing a ceramic-forming material comprising at least one aluminosilicate, the ceramic-forming material having a crystalline content of less than ten percent as determined by x-ray diffraction;
(b) forming the ceramic-forming material into green granules;
(c) sintering the green granules at a temperature of at least 900 degrees Celsius until the crystalline content of the sintered granules is at least ten percent as determined by x-ray diffraction;
(d) providing a bituminous roofing sheet material having an upper surface; and
(e) applying the sintered granules to the upper surface of a bituminous roofing sheet material.
2. A process according to claim 1 , wherein the green granules are sintered until the crystalline content of the granules is at least 90 percent.
3. A process according to claim 2 , wherein the granules are sintered at a temperature of at least 1450 degrees Celsius until the crystalline content of the granules is about 100 percent as determined by x-ray diffraction.
4. A process according to claim 1 , the at least one aluminosilicate comprising kaolin clay.
5. A process according to claim 1 , the at least one aluminosilicate comprising bauxite.
6. A process according to claim 1 , wherein the ceramic-forming material is formed into green granules by mixing the ceramic-forming material with a liquid to form a mixture, the mixture being formed into pellets, and the pellets being screened to provide green granules.
7. A process according to claim 1 , further comprising pressing the sintered granules into the upper surface of the bituminous roofing sheet material to embed the sintered granules in the upper surface of the roofing sheet material.
8. A process according to claim 1 , wherein the ceramic-forming material is formed into green granules having a predetermined particle size distribution.
9. A process according to claim 8 wherein the ceramic-forming material is formed into at least two different size classes of green granules, each class of green granule being characterized by a different predetermined average particle size, the green granules being sintered to provide at least two size classes of sintered granules.
10. A process according to claim 1 , further comprising mixing at least two size classes of granules, each class being characterized by a different particle size distribution.
11. A process according to claim 1 , wherein the shape of the granules and the granule particle size distribution are selected to provide at least 85 percent surface coverage when the roofing granules are applied to upper surface of a bituminous roofing sheet material.
12. A process according to claim 1 wherein the ceramic-forming material is formed into spherical green granules.
13. A process according to claim 1 wherein the ceramic-forming material is formed into platy green granules.
14. A process according to claim 1 further comprising selecting sintered granules from at least two different classes prior to applying the sintered granules in the upper surface of the bituminous roofing sheet material, the sintered granules being selected to provide a predetermined surface coverage of the bituminous sheet material.
15. A process according to claim 14 wherein at least two different classes of sintered granules are applied sequentially to the upper surface of the bituminous sheet roofing material.
16. A process according to claim 14 further comprising mixing the at least two classes of sintered granules prior to applying the sintered granules to the upper surface of the bituminous sheet material.
17. A process according to claim 1 further comprising applying conventional colored roofing granules in the bituminous roofing sheet material.
18. A process according to claim 1 wherein the sintered granules are mixed with a liquid binder composition prior to applying the sintered granules to the upper surface of the bituminous roofing sheet material.
19. A process according to claim 18 wherein the liquid binder composition is selected from the group consisting of acrylic emulsions, acrylic solutions, thermoplastic polymers, fluoropolymer emulsions, epoxy resins, UV curable resins, radiation curable resins, alkaline metal silicates, sol-gel solutions, silicone resins, and silica binders.