Flooded lead-acid battery and method of making the same
Positive active material pastes for flooded deep discharge lead-acid batteries, methods of making the same and lead-acid batteries including the same are provided. The positive active material paste includes lead oxide, a sulfate additive, and an aqueous acid. The positive active material paste contains from about 0.1 to about 1.0 wt % of the sulfate additive. Batteries using such positive active material pastes exhibit greatly improved performance over batteries with conventional positive active material pastes.
1. A flooded lead-acid rechargeable battery comprising:
at least one negative plate;
at least one positive plate comprising in a charged state:
an un-clad cast positive electrode grid made of a lead-antimony alloy; and
a positive paste directly on the grid, the positive paste comprising an oxide of lead and an additive comprising tin or tin oxide, and a molar ratio of lead to the tin or tin oxide of the additive ranges from 450:1 to 650:1; and
an aqueous electrolyte.
2. The battery of claim 1 , wherein the tin exists as an oxide of tin in a charged state.
3. The battery of claim 1 , wherein the lead to tin or tin oxide molar ratio of the positive active paste is 500:1.
4. A flooded lead-acid rechargeable battery comprising:
at least one negative plate;
at least one positive plate comprising in a charged state:
an un-clad cast positive electrode grid made of a lead-antimony alloy; and
a positive paste directly on the grid, the positive paste comprising an oxide of lead and an additive comprising tin or tin oxide, and a weight ratio of lead to the tin or tin oxide of the additive ranges from 800:1 to 1100:1; and
an aqueous electrolyte.
5. The battery of claim 4 , wherein the lead to tin weight ratio of the positive active paste is 900:1.
6. A flooded lead-acid rechargeable battery comprising:
at least one negative plate;
at least one positive plate comprising in a charged state:
an un-clad cast positive electrode grid made of a lead-antimony alloy; and
a positive paste directly on the grid, the positive paste comprising an oxide of lead and an additive comprising tin or tin oxide, the additive being present in the positive paste in an amount ranging from 0.15 wt % to 0.22 wt % on a dry basis; and
an aqueous electrolyte.
7. The battery of claim 6 , wherein the additive is present in the positive paste in an amount of 0.2 wt % on a dry basis.
8. The battery of claim 6 , wherein the additive is present in the positive paste in an amount of 0.18 wt % on a dry basis.