Method of manufacturing active material containing vanadium and method of manufacturing lithium-ion secondary battery containing such active material
The first aspect of the present invention provides a method of manufacturing an active material capable of improving the discharge capacity of a lithium-ion secondary battery. The method of manufacturing an active material in accordance with the first aspect of the present invention comprises the steps of heating a phosphate source, a vanadium source, and water so as to form an intermediate containing phosphorus and vanadium and having a specific surface area of at least 0.1 m 2 /g but less than 25 m 2 /g; and heating the intermediate, a water-soluble lithium salt, and water. The second aspect of the present invention provides a method of manufacturing an active material capable of improving the rate characteristic of a lithium-ion secondary battery. The method of manufacturing an active material in accordance with the second aspect of the present invention comprises the steps of heating a phosphate source, a vanadium source, a water-soluble organic compound, and water for 1 to 12 hr so as to form an intermediate; and heating the intermediate, a lithium salt, and water.
1. A method of manufacturing an active material comprising the steps of;
heating a phosphate source, a vanadium source, and water so as to form, in a mixed liquid, intermediate containing phosphorus and vanadium but not lithium, and having a specific surface area of at least 0.1 m 2 /g but less than 25 m 2 /g; and then to dry the mixed liquid; and
after drying the mixed liquid, heating the intermediate, a water-soluble lithium salt, and water;
thereby forming an active material containing a β-type crystal of LiVOPO 4 .
2. A method of manufacturing an active material according to claim 1 , wherein the specific surface area of the intermediate is 0.4 to 10 m 2 /g.
3. A method of manufacturing an active material according to claim 1 , wherein the water-soluble lithium salt is at least one member selected from the group consisting of LiNO 3 , LiCl, and LiOH.H 2 O.
4. A method of manufacturing a lithium-ion secondary battery, the method comprising the step of forming an electrode having a current collector and an active material layer, disposed on the current collector, containing the active material obtained by the method of manufacturing an active according to claim 1 .
5. A method of manufacturing an active material according to claim 1 , wherein the first heating step dries the mixed liquid in an atmosphere at 150° C. to 300° C.
6. A method of manufacturing an active material according to claim 1 , wherein, before drying, the mixed liquid contains an organic compound or a carbon material.
7. A method of manufacturing an active material according to claim 1 , wherein the water-soluble lithium salt is at least one member selected from the group consisting of LiNO 3 and LiCl.