Enhanced hexagonal ferrite material and methods of preparation thereof
View Patent ↗Embodiments and aspects of the present invention relate to an enhanced hexagonal ferrite magnetic material doped with an alkali metal. The material retains substantial magnetic permeability up to frequencies in the GHz range with low losses. The material may be used in high frequency applications in devices such as transformers, inductors, circulators, and absorbers.
1. An alkali metal-doped hexaferrite having the formula Ba 3-y M x Co 2 Fe 24 O 41 where Ba is barium, M is at least one of potassium and rubidium, Co is cobalt, Fe is iron, O is oxygen, x is greater than zero and less than one, and y is greater than zero and less than or equal to x.
2. The alkali metal-doped hexaferrite of claim 1 wherein M further includes sodium.
3. The alkali metal-doped hexaferrite of claim 2 wherein the at least one of the potassium and rubidium is included in an amount sufficient to impart the alkali metal-doped hexaferrite with a resonant frequency greater than 1 GHz.
4. The alkali metal-doped hexaferrite of claim 1 having an average grain diameter in a range of between about 5 micrometers and about 1 millimeter.
5. The alkali metal-doped hexaferrite of claim 4 wherein the alkali metal-doped hexaferrite comprises a Z-type ferrite.
6. The alkali metal-doped hexaferrite of claim 5 wherein the at least one of the potassium and rubidium is included in an amount sufficient to provide an increased frequency corresponding to a peak of a real component of magnetic permeability of the alkali metal-doped hexaferrite relative to Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
7. The alkali metal-doped hexaferrite of claim 6 wherein the at least one of the potassium and rubidium is included in an amount sufficient to provide an increased frequency corresponding to a peak of an imaginary component of magnetic permeability of the alkali metal-doped hexaferrite relative to Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
8. The alkali metal-doped hexaferrite of claim 7 wherein the at least one of the potassium and rubidium is included in an amount sufficient to provide an increased permeability to permittivity ratio μ r /ε r of the alkali metal-doped hexaferrite at a frequency of at least one of about 0.5 GHz and about 1 GHz relative to Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
9. The alkali metal-doped hexaferrite of claim 8 wherein the at least one of the potassium and rubidium is included in an amount sufficient to provide the Ba 3-y M x Co 2 Fe 24 O 41 with a permeability to permittivity ratio μ r /ε r of greater than about 0.8 at a frequency of at least one of about 0.5 GHz and about 1 GHz.
10. The alkali metal-doped hexaferrite of claim 9 wherein the at least one of the potassium and rubidium is included in an amount sufficient to impart the alkali metal-doped hexaferrite with a real component of relative magnetic permeability greater than about 10 at a frequency above 1 GHz.
11. The alkali metal-doped hexaferrite of claim 10 wherein the at least one of the potassium and rubidium is included in an amount sufficient to impart the alkali metal-doped hexaferrite with a resonant frequency greater than 1 GHz.
12. The alkali metal-doped hexaferrite of claim 1 wherein the at least one of the potassium and rubidium is included in an amount sufficient to increase a frequency corresponding to a peak of a real component of magnetic permeability of the alkali metal-doped hexaferrite relative to Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
13. The alkali metal-doped hexaferrite of claim 1 wherein an amount of the at least one of the potassium and rubidium is sufficient to provide an increased frequency corresponding to a peak of an imaginary component of magnetic permeability of the alkali metal-doped hexaferrite relative to Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
14. The alkali metal-doped hexaferrite of claim 1 wherein the at least one of the potassium and rubidium is included in an amount sufficient to provide an increased permeability to permittivity ratio μ r /ε r of the alkali metal-doped hexaferrite at a frequency of at least one of about 0.5 GHz and about 1 GHz relative to Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
15. The alkali metal-doped hexaferrite of claim 14 wherein the at least one of the potassium and rubidium is included in an amount sufficient to provide the alkali metal-doped hexaferrite with a permeability to permittivity ratio μ r /ε r of greater than about 0.8 at a frequency of at least one of about 0.5 GHz and about 1 GHz.
16. The alkali metal-doped hexaferrite of claim 1 wherein the at least one of the potassium and rubidium is included in an amount sufficient to impart the alkali metal-doped hexaferrite with a real component of relative magnetic permeability at a frequency above 1 GHz greater than that of Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
17. The alkali metal-doped hexaferrite of claim 16 wherein the at least one of the potassium and rubidium is included in an amount sufficient to impart the alkali metal-doped hexaferrite with a real component of relative magnetic permeability greater than about 10 at a frequency above 1 GHz.
18. The alkali metal-doped hexaferrite of claim 1 wherein the at least one of the potassium and rubidium is included in an amount sufficient to impart the alkali metal-doped hexaferrite with a resonant frequency greater than that of Ba 3 Co 2 Fe 24 O 41 not including the at least one of the potassium and rubidium.
19. A method of producing a hexaferrite comprising:
providing a precursor mixture comprising a barium source, a cobalt source, and an iron source;
introducing an alkali metal source to the precursor mixture to produce an alkali metal containing mixture; and
heating the alkali metal containing mixture at a first temperature of at least about 1100° C. for a first period of time sufficient to form hexaferrite particles having the formula Ba 3-y M x Co 2 Fe 24 O 41 where Ba is barium, M is at least one of potassium and rubidium, Co is cobalt, Fe is iron, O is oxygen, x is greater than zero and less than one, and y is greater than zero and less than or equal to x.
20. A method of producing a hexaferrite comprising:
providing a mixture comprising a barium source, a cobalt source, and an iron source;
calcining the mixture at a temperature that is at least about 1100° C. for a period of time sufficient to form hexaferrite particles; and
introducing an alkali metal to the hexaferrite particles in an amount sufficient to provide doped hexaferrite having the formula Ba 3-y M x Co 2 Fe 24 O 41 where Ba is barium, M is at least one of potassium and rubidium, Co is cobalt, Fe is iron, O is oxygen, x is greater than zero and less than one, and y is greater than zero and less than or equal to x.