Method for the production of nanocrystalline nickel oxides

1. Method for the production of a nanocrystalline nickel oxide material comprising the steps of

a) the introduction of a nickel starting compound into a reaction chamber by means of a carrier fluid, wherein the nickel starting compound is an inorganic nickel salt and wherein the nickel starting compound is introduced into the reaction chamber in the form of a solution, slurry, suspension or in solid aggregate state,

b) a thermal treatment of the nickel starting compound in a treatment zone by means of a pulsating flow at a temperature of 200 to 550° C.,

c) the formation of nanocrystalline nickel oxide material, and

d) the discharge of the nanocrystalline nickel oxide material obtained in steps b) and c) from the reactor,

wherein the inorganic nickel salt is selected from the group consisting of nickel nitrate, nickel hydroxide, and a basic nickel carbonate, and

wherein the nickel starting compound has an average particle size of less than 10 μm and is obtained by grinding a suspension of the nickel starting compound.

2. Method according to claim 1 , wherein, in addition to the nickel starting compound, further compounds are also used in the method.

3. Method according to claim 2 , wherein the further compounds are supports or precursors thereof, binders and/or promoters.

4. Method according to claim 3 , wherein aluminium or a transition metal is used as promoter.

5. Method according to claim 4 , wherein the transition metal is selected from the group consisting of W, Pd, Pt, Rh, Ru, Ag, Nb, Cu, Cr, Co, Mo, Fe and Mn.

6. Nanocrystalline nickel oxide material obtained by the method according to claim 1 and having a BET surface area of more than 150 m 2 /q.

7. Nanocrystalline nickel oxide material according to claim 6 , wherein the crystallite size of the nickel oxide lies in the range of from 5 nm to 100 μm.

8. Nanocrystalline nickel oxide material according to claim 6 , having a residual carbon content of less than 50 wt.-%.

9. Nanocrystalline nickel oxide material according to claim 6 , wherein the nickel oxide material is present in pure form, supported, as oxidic mixed compound or as nickel-containing mixture.

10. A method of performing a chemical conversion comprising providing a nanocrystalline nickel oxide material according to claim 6 as catalyst or catalyst precursor.

11. The method according to claim 10 , wherein the chemical conversion is a hydrogenation, a methanation, an alkylation of amines, an amination of alcohols, a polymerization reaction or a Kumada coupling.

12. The method according to claim 10 , wherein the nickel oxide material is reduced to metallic nickel.

13. Catalyst obtained by reduction of the nanocrystalline nickel oxide material according to claim 6 .

14. A method for the production of a nanocrystalline nickel oxide material comprising:

a) grinding a suspension of an inorganic nickel salt to obtain a nickel starting compound having an average particle size of less than 10 μm;

b) introducing the nickel starting compound into a reaction chamber by means of a carrier fluid, wherein the nickel starting compound is provided in solution, as a slurry, in suspension or in solid aggregate state;

c) thermally treating the nickel starting compound in a treatment zone by means of a pulsating flow at a temperature of 200 to 550° C. to form a nanocrystalline nickel oxide material; and,

d) discharging the nanocrystalline nickel oxide material,

wherein the inorganic nickel salt is selected from the group consisting of nickel nitrate, nickel hydroxide, and a basic nickel carbonate.