Method for purifying elemental boron
Elemental boron with a boron content of at least 96.8% by weight, an oxygen content of at most 1.6% by weight, a nitrogen content of at most 0.2% by weight, a crystallinity of 30% by weight or less, and a particle size distribution with a d100 value of 9 μm or less.
1. Elemental boron with a boron content of at least 96.8% by weight, an oxygen content of at most 1.6% by weight, a nitrogen content of at most 0.2% by weight, a crystallinity of 30% by weight or less, a particle size distribution with a d100 value of 9 μm or less, and a content of at least one metallic impurity of 0.1 wt.-% to at most 1.0 wt.-%,
wherein, the at least one metallic impurity includes at least one metal of the fourth period of the Periodic Table of Elements in an amount of from 0.1 wt.-% to at most 0.2 wt.-%,
wherein, potassium is present in an amount of from 0.1 wt.-% to less than 0.3 wt.-%.
2. Elemental boron as recited in claim 1 , wherein the elemental boron has a content of anionic impurities of at most 0.4% by weight.
3. Elemental boron as recited in claim 2 , where the anionic impurities are at least one of chloride and fluoride, and the content of the anionic impurities is at most 0.2% by weight for each of the at least one of chloride and fluoride.
4. Elemental boron as recited in claim 1 , wherein the at least one metallic impurity further includes at least one of an alkali metal and an alkaline earth metal, which are respectively not also a metal of the fourth period of the Periodic Table of Elements.
5. Elemental boron as recited in claim 4 , wherein the alkali metal is present in an amount of at most 0.4 wt.-% including potassium.
6. Elemental boron as recited in claim 1 , wherein the metal of the fourth period of the Periodic Table of Elements is iron.
7. Elemental boron as recited in claim 4 , wherein the alkaline earth metal is magnesium present in an amount of up to 0.4 wt. %.
8. A purified elemental boron obtainable by a method comprising:
providing an elemental boron;
milling the elemental boron in the presence of an alcohol so as to obtain a first suspension;
adding a strong acid which is soluble in the alcohol to the first suspension so as to obtain a second suspension;
heating the second suspension to boiling with reflux cooling so as to obtain a third suspension;
separating off a solid in the third suspension; and
heat-treating the solid under reduced pressure so as to provide the purified elemental boron,
wherein the purified elemental boron has a boron content of at least 96.8% by weight, an oxygen content of at most 1.6% by weight, a nitrogen content of at most 0.2% by weight, a crystallinity of 30% by weight or less, a particle size distribution with a d100 value of 9 μm or less, and a content of at least one metallic impurity of 0.1 wt.-% to at most 1.0 wt.-%,
wherein, the at least one metallic impurity includes at least one metal of the fourth period of the Periodic Table of Elements in an amount of from 0.1 wt.-% to at most 0.2 wt.-%,
wherein, potassium is present in an amount of from 0.1 wt.-% to less than 0.3 wt.-%.