Radio-opaque marker for medical implants
A radio-opaque marker for medical implants comprising between 10 and 90 weight percent of a biodegradable base component, between 10 and 90 weight percent of one or more radio-opaque elements selected from the consisting of I, Au, Ta, Y, Nb, Mo, Ru, Rh, Ba, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Hf, Ta, W, Re, Os, Ir and Bi as a marker component and 10 weight percent of residual components, the aforementioned components amounting to 100 weight percent.
1. A radiopaque marker for medical implants comprising:
a) 10 to 90 weight-percent of a biodegradable base component consisting essentially of an alloy and capable of degrading in situ over a medically useful period of time;
b) 10 to 90 weight-percent of a marker component comprising one or more radiopaque elements selected from the group consisting of I, Au, Ta, Y, Nb, Mo, Ru, Rh, Ba, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Hf, W, Re, Os, Ir, and Bi, wherein the radiopaque elements comprise at lest 90 weight-percent Ta, the marker component comprising fine particles; and,
c) less than or equal to 10 weight-percent residual components,
the components cited adding up to 100 weight-percent, wherein as the base component degrades the marker component particles are excreted without appreciable absorption into surrounding tissue.
2. The marker of claim 1 , wherein the biodegradable base component consists essentially of one or more biodegradable elements selected from the group consisting of magnesium, iron, and zinc.
3. The marker of claim 1 , wherein the marker component comprises one or more elements selected from the group consisting of I, Ta, Y, Ce, Nd, Sm, Gd, and Dy.
4. The marker of claim 1 , wherein a proportion of the radiopaque elements Y, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu as components of the marker component is not more than 10 weight-percent in the marker.
5. A biodegradable implant having a section or coating incorporating a radiopaque marker, the section or coating incorporating the radiopaque marker comprising:
a) 30 to 70 weight-percent of a base component consisting essentially of a biodegradable alloy capable of degrading in situ over a medically useful period of time;
b) 30 to 70 weight-percent of a marker component comprising one or more radiopaque elements selected from the group consisting of I, Au, Ta, Y, Nb, Mo, Ru, Rh, Ba, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Hf, W, Re, Os, Ir, and Bi, wherein the radiopaque elements comprise at least 90 weight-percent Ta, the marker component comprising fine particles; and,
c) less than or equal to 10 weight-percent residual components,
the components cited adding up to 100 weight-percent wherein as the base component degrades the marker component particles are excreted without appreciable absorption into surrounding tissue.
6. A biodegradable implant comprising:
a) a main body; and
b) a radiopaque marker at least partially comprising the main body, the radiopaque marker comprising
(i) 10 to 90 weight-percent of a base component consisting essentially of a biodegradable alloy;
(ii) 10 to 90 weight-percent of one or more radiopaque elements selected from the group consisting of I, Au, Ta, Y, Nb, Mo, Ru, Rh, Ba, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu, Hf, W, re, Os, Ir, and Bi, wherein the radiopaque elements comprise at least 90 weight-percent Ta, the marker component comprising fine particles; and,
(iii) less than or equal to 10 weight-percent residual components, the components cited adding up to 100 weight-percent wherein as the base component degrades the marker component particles are excreted without appreciable absorption into surrounding tissue.
7. The marker of claim 1 , wherein a proportion of the rare earth elements and of yttrium as components of the marker component is less than or equal to 10 weight-percent, in the marker.
8. The marker of claim 6 , wherein the implant has a plurality of cavities formed therein and the radiopaque marker is at least partially disposed within the cavities.
9. The marker of claim 1 , wherein the fine particles, when dispersed in situ, are in contact with body material.
10. The marker of claim 1 wherein the base component is present in an amount of 40 to 60 weight-percent.
11. The implant of claim 5 wherein the radiopaque marker is a coating.
12. The implant of claim 11 wherein the coating has a thickness in a range of approximately 5 μm to 100 μm.
13. The implant of claim 11 wherein the coating is applied terminally to the implant.
14. The implant of claim 5 wherein the base component is present in an amount of 30 to 70 weight-percent.
15. The implant of claim 6 wherein the base component is present in an amount of 30 to 70 weight-percent.
16. A radiopaque marker for medical implants comprising:
a) 10 to 90 weight-percent of a biodegradable base component consisting essentially of an alloy and capable of degrading in situ over a medically useful period of time;
b) 10 to 90 weight-percent of a marker component comprising at least 90 weight-percent of Ta, the marker component comprising fine particles; and,
c) less than or equal to 10 weight-percent residual components, the components cited adding up to 100 weight-percent, wherein as the base component degrades the marker component particles are excreted without appreciable absorption into surrounding tissue.
17. A biodegradable implant having a section or coating incorporating a radiopaque marker, the section or coating incorporating the radiopaque marker comprising:
a) 10 to 90 weight-percent of a base component consisting essentially of a biodegradable alloy capable of degrading in situ over a medically useful period of time;
b) 10 to 90 weight-percent of a marker component comprising at least 90 weight-percent of Ta, the marker component comprising fine particles; and,
c) less than or equal to 10 weight-percent residual components, the components cited adding up to 100 weight-percent wherein as the base component degrades the marker component particles are excreted without appreciable absorption into surrounding tissue.
18. A biodegradable implant comprising:
a) a main body; and
b) a radiopaque marker at least partially comprising the main body, the radiopaque marker comprising
(i) 10 to 90 weight-percent of a base component consisting essentially of a biodegradable alloy;
(ii) 10 to 90 weight-percent of one or more radiopaque elements wherein the radiopaque elements comprise at least 90 weight-percent Ta, the marker component comprising fine particles; and,
(iii) less than or equal to 10 weight-percent residual components, the components cited adding up to 100 weight-percent wherein as the base component degrades the marker component particles are excreted without appreciable absorption into surrounding tissue.