Composite wood board
In a stack of composite wood boards, the wood boards comprise wood particles and an organic binder.
1. A composite wood board comprising a collection of wood held together by an organic binder, wherein the organic binder includes at least one reaction product of:
i) a reducing sugar reactant selected from the group consisting of: a reducing sugar; a reducing sugar yielded by a carbohydrate in situ under thermal curing conditions; and combinations thereof; and
ii) an amine reactant selected from a primary amine NH 2 R 1 and a secondary amine NHR 1 R 2 , where R 1 and R 2 are each independently selected in NHR 1 R 2 , R 1 is alkyl which is substituted by at least one group selected from aminoalkyl, amide, nitrile, amino, dialkylamino, acylamino and combinations thereof, and R 2 is selected from alkyl, cycloalkyl, alkenyl, cycloalkenyl, heterocyclyl, aryl, and heteroaryl, each of which may be optionally substituted; and
where the composite wood board has one or more of the following characteristics:
a modulus of elasticity (MOE) of at least 1800 N/mm 2 ,
a bending strength (MOR) of at least 14 N/mm 2
an Internal bond strength (IB) of at least 0.28 N/mm 2
a thickness swelling after 24 hours in water at 20° C. of less than or equal to 12%
a water absorption after 24 hours in water at 20° C. of less than or equal to 40%.
2. A composite wood board in accordance with claim 1 , in which the binder is substantially formaldehyde free.
3. A composite wood board in accordance with claim 1 , in which the board has a modulus of elasticity (MOE) of at least 1800 N/mm 2 .
4. A composite wood board in accordance with claim 1 , in which the board has a modulus of elasticity (MOE) of at least 2500 N/mm 2 .
5. A composite wood board in accordance with claim 1 , in which the board has a bending strength (MOR) of at least 14 N/mm 2 .
6. A composite wood board in accordance with claim 1 , in which the board has a bending strength (MOR) of at least 18 N/mm 2 .
7. A composite wood board in accordance with claim 1 , in which the board has an Internal bond strength (IB) of at least 0.28 N/mm 2 .
8. A composite wood board in accordance with claim 1 , in which the board has an Internal bond strength (IB) of at least 0.4 N/mm 2 .
9. A composite wood board in accordance with claim 1 , in which the boards has a Thickness swelling after 24 hours in water at 20° C. of less than or equal to 10%.
10. A composite wood board in accordance with claim 1 , in which board has a water absorption after 24 hours in water at 20° C. of less than or equal to 30%.
11. A composite wood board in accordance with claim 1 , in which the board is a wood particle board.
12. A wood board in accordance with claim 1 , in which the board is an orientated strand board.
13. A composite wood board in accordance with claim 1 , in which the board is a fibre board.
14. A composite wood board in accordance with claim 1 , in which the board has a resin content (weight of dry resin to weight of dry wood particles) in the range 8 to 18% by weight.
15. A composite wood board in accordance with claim 1 , in which the board has a binder which comprises at least one Maillard reaction product.
16. A composite wood board in accordance with claim 1 , in which the board comprises wax.
17. A composite wood board in accordance with claim 16 , in which the board comprises wax in the range 0.1 to 2% by weight, preferably 0.5 to 1% by weight.
18. A composite wood board in accordance with claim 1 , wherein the organic binder is a reaction product of curing an aqueous binder solution in which the ratio of the number of moles of the amine reactant to the number of moles of the reducing sugar ranges from about 1:4 to about 1:15.
19. A composite wood board in accordance with claim 1 , wherein the organic binder is a reaction product of curing an aqueous binder solution in which the percent by dry weight of the reducing sugar reactant(s) with respect to the total weight of reactants in the aqueous binder solution ranges from about 74% to about 91%.
20. A composite wood board comprising a collection of wood held together by an organic binder, wherein the organic binder is substantially formaldehyde free and includes at least one reaction product of:
i) a reducing sugar reactant selected from the group consisting of: a reducing sugar; a reducing sugar yielded by a carbohydrate in situ under thermal curing conditions; and combinations thereof; and
ii) an amine reactant selected from a primary amine NH 2 R 1 and a secondary amine NHR 1 R 2 , where R 1 and R 2 are each independently selected in NHR 1 R 2 , R 1 is alkyl which is substituted by at least one group selected from aminoalkyl, amide, nitrile, amino, dialkylamino, acylamino and combinations thereof, and R 2 is selected from alkyl, cycloalkyl, alkenyl, cycloalkenyl, heterocyclyl, aryl, and heteroaryl, each of which may be optionally substituted; and
wherein the organic binder is a reaction product of curing an aqueous binder solution in which the percent by dry weight of the reducing sugar reactant(s) with respect to the total weight of reactants in the aqueous binder solution ranges from about 74% to about 91%, and
where the composite wood board has:
a modulus of elasticity (MOE) of at least 1800 N/mm 2 , and
a bending strength (MOR) of at least 14 N/mm 2 , and
an Internal bond strength (IB) of at least 0.28 N/mm 2 , and
a thickness swelling after 24 hours in water at 20° C. of less than or equal to 12%, and
a water absorption after 24 hours in water at 20° C. of less than or equal to 40%, and
a resin content (weight of dry resin to weight of dry wood particles) in the range 8 to 18% by weight.