Method for applying a powder coating
A method for the application of at least two different powder coating layers to a substrate comprising the steps of application of a first powder coating layer followed by the application of a second powder coating layer, without any substantial curing of the first powder coating layer prior to the application of the second powder coating layer, followed by the simultaneous curing of the first powder coating layer and the second powder coating layer, wherein the first powder coating layer is applied to the substrate using a corona charging system and the second powder coating layer is applied to the substrate using a tribo charging system, or the first powder coating layer is applied to the substrate using a tribo charging system and the second powder coating layer is applied to the substrate using a corona charging system and the first powder coating layer and second powder coating layer have an opposite electrostatic polarity.
1. A method for the application of at least two different powder coating layers to a substrate comprising the steps of application of a first powder coating layer followed by the application of a second powder coating layer, without any substantial curing of the first powder coating layer prior to the application of the second powder coating layer, followed by the simultaneous curing of the first powder coating layer and the second powder coating layer, wherein
the first powder coating layer is applied to the substrate using a corona charging system and the second powder coating layer is applied to the substrate using a tribo charging system,
or
the first powder coating layer is applied to the substrate using a tribo charging system and the second powder coating layer is applied to the substrate using a corona charging system, and
wherein the first powder coating layer and second powder coating layer have an opposite electrostatic polarity, and
wherein the first powder coating layer comprises a polyester film-forming resin.
2. The method according to claim 1 wherein the first powder coating layer is applied having a negative polarity using the corona charging system and the second powder coating layer is applied having a positive polarity using the tribo charging system,
or
the first powder coating layer is applied having a positive polarity using the tribo charging system and the second powder coating layer is applied having a negative polarity using the corona charging system.
3. The method according to claim 1 wherein the corona charging system is charged to a potential of between 30 and 100 kV.
4. The method according to claim 3 wherein the corona charging system is charged to a potential of between 70 and 100 kV.
5. The method according to claim 1 wherein the first or the second powder coating layer is applied using the corona charging system at an application rate between 100 and 300 g/min.
6. The method according to claim 1 wherein the first or the second powder coating layer is applied using the tribo charging system at an application rate between 100 and 300 g/min.
7. The method according to claim 2 wherein the corona charging system is charged to a potential of between 30 and 100 kV.
8. The method according to claim 7 wherein the corona charging system is charged to a potential of between 70 and 100 kV.
9. The method according to claim 2 wherein the first or the second powder coating layer is applied using the corona charging system at an application rate between 100 and 300 g/min.
10. The method according to claim 3 wherein the first or the second powder coating layer is applied using the corona charging system at an application rate between 100 and 300 g/min.
11. The method according to claim 4 wherein the first or the second powder coating layer is applied using the corona charging system at an application rate between 100 and 300 g/min.
12. The method according to claim 7 wherein the first or the second powder coating layer is applied using the corona charging system at an application rate between 100 and 300 g/min.
13. The method according to claim 8 wherein the first or the second powder coating layer is applied using the corona charging system at an application rate between 100 and 300 g/min.
14. The method according to claim 2 wherein the first or the second powder coating layer is applied using the tribo charging system at an application rate between 100 and 300 g/min.
15. The method according to claim 3 wherein the first or the second powder coating layer is applied using the tribo charging system at an application rate between 100 and 300 g/min.
16. The method according to claim 4 wherein the first or the second powder coating layer is applied using the tribo charging system at an application rate between 100 and 300 g/min.
17. The method according to claim 5 wherein the first or the second powder coating layer is applied using the tribo charging system at an application rate between 100 and 300 g/min.
18. The method according to claim 7 wherein the first or the second powder coating layer is applied using the tribo charging system at an application rate between 100 and 300 g/min.
19. The method according to claim 8 wherein the first or the second powder coating layer is applied using the tribo charging system at an application rate between 100 and 300 g/min.
20. The method according to claim 10 wherein the first or the second powder coating layer is applied using the tribo charging system at an application rate between 100 and 300 g/min.