Catalyst, process for producing the catalyst, use of the catalyst

1. A catalyst for oxidation of exhaust gas constituents including nitrogen oxide, the catalyst comprising:

a particulate support material composed of titanium-containing nanoparticles;

a platinum coating, wherein the support material is coated with the platinum coating; and

bridges arranged between and joining at least one of a plurality of platinum particles of the platinum coating and a plurality of support material particles of the support material, the bridges containing metal oxide and at least one of silicon and tungsten.

2. The catalyst according to claim 1 , wherein the catalyst oxidizes nitrogen monoxide, the particulate support material is composed of titanium dioxide nanoparticles, and the platinum coating is composed of platinum particles.

3. The catalyst according to claim 1 , wherein the platinum coating is composed of platinum nanoparticles.

4. The catalyst according to claim 1 , wherein the catalyst further includes palladium.

5. The catalyst according to claim 1 , wherein the catalyst has a platinum concentration in the range of 0.5 mg to 150 mg per 1 gram of catalyst weight.

6. The catalyst according to claim 1 , wherein the catalyst has a platinum concentration in the range of 1 mg to 100 mg per 1 gram of catalyst weight.

7. The catalyst according to claim 1 , wherein the catalyst has one of:

a titanium:silicon ratio of 20:1 to 2:1; and

a titanium:tungsten ratio of 80:1 to 8:1.

8. A process for producing a catalyst according to claim 1 , comprising the following steps:

providing a titanium-containing first precursor material for production of a support material;

providing a second precursor material for production of a catalytically active component, the second precursor material comprising at least one of platinum and palladium;

providing a third precursor material containing at least one of silicon, tungsten, and palladium, for production of a stabilizing material;

introducing the titanium-containing first precursor material into a through-flowable reaction zone of a pyrolysis device;

introducing the second precursor material into the reaction zone downstream of where the first precursor material is introduced; and

introducing the third precursor material into the reaction zone one of:

simultaneously with the introduction of the first precursor material;

downstream of where the first precursor material is introduced;

downstream of where the second precursor material is introduced.

9. The process according to claim 8 , wherein:

the first precursor material comprises one of titanium halides, titanium acetates, titanium tetraisopropoxide, and titanium alkoxides;

the second precursor material comprises one of platinum compounds and palladium compounds; and

the third precursor material comprises one of silicon compounds, tungsten compounds, and palladium compounds including palladium chlorides.

10. The process according to claim 8 , wherein:

the first precursor material comprises one of TiCl 4 , Ti(NO 3 ) 2 , or Ti(SO 4 ) 2 , titanium acetates, titanium tetraisopropoxide, and titanium tetraethoxide;

the second precursor material comprises one of platinum chlorides, platinum acetates, tetraammineplatinum hydroxide, platinum alkoxides, platinum nitrate, and palladium chlorides; and

the third precursor material comprises one of silicon halides, silicon chlorides, silanes, hexamethyldisiloxane, silicon alkoxides, tungsten halides, tungstates, tungsten alkoxides, tungsten acetates, tungsten nitrate; and palladium chlorides.

11. The process according to claim 8 , wherein the third precursor material is one of a silicon compound and a tungsten compound; and

at least one of the first and third precursor material is introduced into the reaction zone in or essentially together with an oxidizing atmosphere.

12. The process according to claim 11 , wherein the oxidizing atmosphere is obtained by an addition of a gaseous oxidizing agent.

13. The process according to claim 8 , wherein the second precursor material is introduced into the reaction zone in or essentially together with a reducing atmosphere.

14. The process according to claim 13 , wherein the reducing atmosphere is obtained by an addition of a gaseous reducing agent to the reaction zone.

15. The process according to claim 14 , wherein the gaseous reducing agent is one of hydrogen and methane.

16. A process of oxidizing exhaust gas constituents, comprising the step of using a catalyst according to claim 1 for oxidation of exhaust gas constituents including nitrogen oxide downstream of an internal combustion engine.

17. The process according to claim 16 , wherein the step of using is for oxidation of nitrogen monoxide.

18. A coating comprising a catalyst according to claim 1 useful for application to ceramic or metallic catalyst substrates.