Fibrous pulp and use thereof in a composite
View Patent ↗A composition comprises (i) an elastomer, (ii) from 1 to 5 volume % of fibrous pulp, the pulp having a specific surface area of from 7 to 11 sq.m./g and the fiber having a fiber length of from 0.5 to 1.1 mm, a tensile modulus of from 2.5 to 130 GPa, and a tensile strength of from 1 to 3 GPa, and (iii) from 5 to 14 volume % of yield-strain promoter in the form of fibers, needles, powder or platelets, wherein the composition has a yield strain of at least 70%, an elongation at break of at least 200%, and a yield stress of at least 4 MPa.
1. A composition comprising:
(i) an elastomer,
(ii) from 1 to 5 volume % of fibrous pulp which is p-aramid, the pulp having a specific surface area of from 7 to 11 sq.m./g and the fiber having a fiber length of from 0.5 to 1.1 mm, a tensile modulus of from 2.5 to 130 GPa, and a tensile strength of from 1 to 3 GPa, and
(iii) from 5 to 14 volume % of yield-strain promoter which is clay in the form of fibers or needles,
wherein the composition has a yield strain of at least 95%, an elongation at break of at least 200%, and a yield stress of at least 4 MPa.
2. The composition of claim 1 , wherein the yield-strain promoter comprises from 6 to 13 volume % of the composition.
3. The composition of claim 2 , wherein the yield strain promoter comprises from 8 to 12 volume % of the composition.
4. A tire, conveyor belt or power transmission belt comprising the composition of claim 1 .
5. The composition of claim 1 , wherein the clay is sepiolite, attapulgite or montmorillonite.