Composite edge for producing double or multiple pane insulation glass or solar modules
View Patent ↗An edge seal for manufacturing two-pane or multi-pane insulating glass or solar modules having a primary sealant and a secondary sealant has the following overall composition: a) 30-60 wt. %, preferably 40-50 wt. %, olefinic polymers, Mn 400-600,000 D, preferably 5,000-300,000 D b) 2-35 wt. %, preferably 5-25 wt. %, modified polymer c) 5-40 wt. %, preferably 10-30 wt. %, fine-particle, inert fillers d) 5-25 wt. %, preferably 10-15 wt. %, desiccants and water scavengers 0-3 wt. % aging resistors, in particular anti-oxidants or UV stabilizers.
1. An edge seal for manufacturing two-pane or multi-pane insulating glass or solar modules, the edge seal including a primary sealant composition and a secondary sealant composition, wherein the primary sealant composition comprises:
a) a modified polymer with special reactive groups;
b) olefinic polymers of Mn 400-600,000 D, or combinations thereof included in an amount from about 32% to 60% by weight of the total primary sealant composition;
c) at least one fine-particle inert filler included in an amount from about 10% to 40% by weight of the total primary sealant composition; wherein the at least one fine-particle inert filler comprises a carbon black included in an amount from 5% to 20% by weight of the total primary sealant composition, wherein the carbon black is oxidatively post-treated by a furnace process and has a particle size ranging from 50 nm to 60 nm resulting in the primary sealant having a volume resistivity of >1010 Ohm·cm;
d) at least one of a desiccant and water scavenger included in an amount from 5% to 25% by weight of the total primary sealant composition; and
e) at least one aging resistor including an anti-oxidant or UV stabilizer included in an amount from about 0.1% to 3% by weight of the total primary sealant composition.
2. The edge seal of claim 1 , wherein the modified polymer with reactive groups is included in an amount from about 5% to 35% by weight of the total primary sealant composition.
3. The edge seal of claim 2 , wherein the at least one filler further includes a fine particle filler selected from the group consisting of ground and precipitated chalks, silicates, silicon oxides and carbon blacks that are different from the oxidatively post-treated carbon black.