High-characteristic steel for large-size parts
High-strength steel of which the chemical composition comprises, by weight: 0.03%≦C<0.2% Si≦0.49% 3%<Mn≦4% Ni≦0.9% 1%≦Cr≦5% Mo+W/2≦1% Cu≦0.9% S+Se/2+Te/3<0.020% Al≦0.1%, the remainder being iron and impurities resulting from production. Block and plates obtained.
1. Steel block or plate having a thickness greater than or equal to 20 mm and less than or equal to 1 m, and a composition-comprising, by weight:
0.03%≦C≦0.15%
Si≦0.49%
3.2%≦Mn≦4%
Ni≦0.9%
1%≦Cr≦5%
Mo+W/2≦1%
Cu≦0.9%
S+Se/2+Te/3<0.020%
Al≦0.1%,
the remainder being iron and impurities resulting from production;
wherein the steel block or plate has a structure consisting of bainite and martensite, and in that the difference in Brinell hardness between the harder regions and the less hard regions of the steel block or plate, resulting from segregated veins, is less than 20% of the average Brinell hardness of the steel block or plate.
2. Steel block or plate according to claim 1 , wherein the chemical composition is such that: Cr>2.5%.
3. Steel block or plate according to claim 1 , wherein Cr<0.5%.
4. Steel block or plate according to claim 1 , wherein Ni<0.5%.
5. Steel block or plate according to claim 1 , wherein Cu<0.4%.
6. Steel block or plate according to claim 1 , wherein Mo+W/2≦0.3%.
7. Steel block or plate according to claim 1 , wherein the chemical composition is such that: 2.7%≦Cr≦3% and Mo≦0.3%.