Two part sizing composition for coating glass fibres and composite reinforced with such glass fibres
A pellet comprising glass fibers and a thermoplastic polyester matrix, wherein the glass fiber at least partially has been coated with a two-part sizing composition comprising: (C) A precursor comprising: (a) an aminosilane and (b) a polymer or copolymer containing carboxylic acid and/or anhydride, both having a functionality, F≧3, and (D) A binder comprising a multifunctional epoxy resin of functionality, F≧3, and wherein the pellet has been subjected to a solid state post condensation process (SSPC).
1. A pellet comprising glass fibres and a thermoplastic polyester matrix, wherein the glass fibres are at least partially coated with a two-part sizing composition comprising:
(A) a precursor comprising:
(a) an aminosilane and
(b) a polymer or copolymer containing carboxylic acid and/or anhydride, both having a functionality, F≧3, and
(B) a binder comprising a multifunctional epoxy resin of functionality, F≧3, and wherein the pellet has been subjected to a solid state post condensation process (SSPC).
2. A pellet comprising glass fibres and a polyester matrix, wherein the glass fibres are at least partially coated with a two-part sizing composition comprising:
(A) a precursor comprising:
(a) an aminosilane, and
(b) a polymer or copolymer containing carboxylic acid and/or anhydride, both having a functionality, F≧3, and
(B) a binder comprising a multifunctional epoxy resin of functionality, F≧3, wherein the polyester matrix is a thermoplastic polyester containing a stabilizer selected from
(i) polycarbodiimide and/or=(ii) an epoxy group containing stabilizer.
3. A pellet according to claim 1 , wherein the anhydride contained in said polymer or copolymer (b) is maleic anhydride, and/or the carboxilic acid contained in said polymer or copolymer (b) is acrylic acid.
4. A pellet according to claim 1 , wherein said multifunctional epoxy resin comprises a novolac type epoxy.
5. A pellet according to claim 1 , wherein the aminosilane is selected from one or more of an aminodialkoxysilane and/or aminotrialkoxysilane.
6. A pellet according to claim 1 , wherein the sizing further comprises at least one additive selected from the group consisting of filmformers, Ph adjusters, a non-ionic lubricants, cationic lubricants, antistatic agents, anti-foaming agents, isocyanate based cross-linkers and boron compounds.
7. A pellet according to claim 1 , wherein the thermoplastic polyester matrix is polyethylene terephthalate (PET).
8. A pellet according to claim 1 , wherein the thermoplastic polyester matrix is a thermoplastic polyester containing a stabilizer selected from (i) polycarbodiimide and/or (ii) an epoxy group containing stabilizer.
9. A pellet according to claim 8 , wherein the epoxy group containing stabilizer is an epoxidized fatty acid ester or ether.
10. A pellet according to claim 1 , wherein the thermoplastic polyester matrix is a thermoplastic polyester comprising an inorganic nucleating agent.
11. A process for producing a pellet according to claim 1 , comprising:
(a) blending in an extruder the glass fibres with the thermoplastic polyester matrix to form glass fibre reinforced polyester pellets; and
(b) subjecting the pellets to a solid state post condensation process (SSPC).
12. The process according to claim 11 , wherein the solid state post condensation step (b) is carried out at a temperature comprised between 160° C. and 245° C.
13. The process according to claim 11 , which further comprises adding a stabilizer to the glass fibre reinforced polyester pellets after conducting the SSPC.