Self-sensitive polymerizable liquid resin and use thereof
A self-sensitive polymerizable liquid resin is provided, which contains an uncrosslinked Michael addition reaction product of the following components: a Michael donor, a Michael accepter and optionally a viscosity modifier. The Michael accepter has 5 to 18 acryloyl functional groups. The self-sensitive polymerizable liquid resin of the present invention is capable of being used as an aid in a coating composition and providing a good property in deep radiation curing, and is particularly applicable in color coatings.
1. A self-sensitive polymerizable liquid resin, comprising an uncrosslinked Michael addition reaction product of the following components:
(a) a Michael donor;
(b) a Michael acceptor; and
(c) a viscosity modifier;
wherein the Michael acceptor (b) has 5 to 18 acryloyl functional groups; and the molar ratio of (a) to (b) is in a range of 1:2 to 1:100, wherein the Michael donor is a β-dicarbonyl compound, wherein the viscosity modifier forms a covalent bond with the Michael donor at a terminal of the resin.
2. The self-sensitive polymerizable liquid resin according to claim 1 , having a viscosity of 50 to 30000 cps at 60° C.
3. The self-sensitive polymerizable liquid resin according to claim 1 , wherein the Michael acceptor is an acrylate compound having 5 to 18 acryloyl functional groups.
4. The self-sensitive polymerizable liquid resin according to claim 1 , wherein the content of the Michael donor is approximately 1 wt % to 40 wt %, based on the total weight of the self-sensitive polymerizable liquid resin.
5. The self-sensitive polymerizable liquid resin according to claim 1 , wherein the content of the Michael acceptor is approximately 50 wt % to 99 wt %, based on the total weight of the self-sensitive polymerizable liquid resin.
6. The self-sensitive polymerizable liquid resin according to claim 1 , wherein the content of the viscosity modifier is sufficient to avoid gelation caused by over-crosslinking during a Michael addition reaction involving the Michael acceptor and the Michael donor and up to approximately 40 wt %, based on the total weight of the self-sensitive polymerizable liquid resin.
7. The self-sensitive polymerizable liquid resin according to claim 6 , wherein the viscosity modifier comprises a monofunctional or bifunctional acrylic monomer, a monofunctional or bifunctional acrylate monomer or a mixture thereof.
8. The self-sensitive polymerizable liquid resin according to claim 1 , wherein the β-dicarbonyl compound is selected from the group consisting of ethyl acetoacetate, methyl acetoacetate, 2-ethylhexylacetoacetate, laurylacetoacetate, tert-butyl acetoacetate, allylacetoacetate, benzylacetoacetate, isobutylacetoacetate, 2-methoxyethyl acetoacetate, 1,4-butanediol diacetoacetate, 1,6-hexane diol diacetoacetate, neopentyl glycol diacetoacetate, cyclohexanedimethanol diacetoacetate, ethoxylated bisphenol A diacetoacetate, trimethylolpropane triacetoacetate, polycaprolactone triacetoacetate, pentaerythritol tetraacetoacetate, acetoacetanilide, N-alkyl acetoacetanilide, acetoacetamide, 2-acetoacetoxyethyl acrylate, 2-acetoacetoxyethyl methacrylate, pentane-2,4-dione, hexane-2,4-dione, heptane-3,5-dione, dibenzoylmethane, diethyl methylmalonate, diethyl isopropylmalonate, cycloisopropyl (isopropylidenyl) malonate, 5,5-dimethylcyclohexane-1,3-dione, cyclopentane-1,3-dione, cyclohexane-1,3-dione, cycloheptane-1,3-dione, cyclooctane-1,3-dione, 2-acetylcyclopentatone, 2-acetylcyclohexanone, 2-acetylcycloheptanone, 2-acetylcyclooctanone and a mixture thereof.
9. The self-sensitive polymerizable liquid resin according to claim 1 , having a viscosity of 50 to 15000 cps at 60° C.
10. The self-sensitive polymerizable liquid resin according to claim 1 , wherein the content of the viscosity modifier is approximately 1 to 30 wt %, based on the total weight of the self-sensitive polymerizable liquid resin.
11. A coating composition, comprising the self-sensitive polymerizable liquid resin according to claim 1 .
12. The coating composition according to claim 7 , further comprising a carrier resin, a dilution monomer and, optionally, a coloring material.
13. The coating composition according to claim 11 , comprising the coloring material.
14. The coating composition according to claim 12 , wherein the coating composition does not contain a solvent.
15. The coating composition according to claim 12 , wherein the coating composition does not contain a photo initiator.
16. The coating composition according to claim 12 , wherein the coating composition contains a photo initiator.
17. A film, comprising:
a subsrate; and a coating formed by the coating composition according to claim 11 on at least one surface of the substrate.