A gold alloy having, expressed by weight, about 24.5 to 25.5% Au, about 19.0 to 23.0% Ag, about 43.0 to 47.0% Cu, about 6.0 to 10.0% Zn, about 0.05 to 0.30% Si, and about 0.005 to 0.03% Ir. Alternatively, a alloy having, expressed by weight, about 16-17% Au, about 19-23% Ag, about 50-55% Cu, about 6-10% Zn, about 0.05-0.30% Si, and about 0.005-0.03% Ir.
1. A very low karat gold alloy comprising, expressed by weight:
no less than 24.5% Au;
no less than 19.0% Ag;
no less than 43.0% Cu;
no less than 6.0% Zn;
no less than 0.05% Si; and
no less than 0.005% Ir.
2. A very low karat gold alloy comprising, expressed by weight:
about 24.5 to 25.5% Au;
about 19.0 to 23.0% Ag;
about 43.0 to 47.0% Cu;
about 6.0 to 10.0% Zn;
about 0.05 to 0.30% Si; and
about 0.005 to 0.03% Ir.
3. The alloy of claim 2 comprising, expressed by weight:
about 25.0% Au;
about 21.0% Ag;
about 44.9% Cu;
about 8.83% Zn;
about 0.17% Si; and
about 0.02% Ir.
4. The alloy of claim 2 , wherein the alloy has CIELab coordinate values of about 89.0 to 90.0 L, about 1.5 to 2.5 a, about 17.5 to 18.5 b, about 17.5 to 19.0 c, and about 34.0 to 35.5 YI.
5. The alloy of claim 2 , wherein the alloy has a tarnish-resistance value of about 15 to 30 DE by sulfur and about 35 to 45 DE by chlorine.
6. The alloy of claim 2 , wherein the alloy has an annealed hardness of about 120 to 130 HV 0,2 when annealed by heating to a temperature of about 600° C. in a non-oxidizing atmosphere, held at that temperature for about 30 minutes, and then quenched in water; and about 130 to 180 HV 0,2 when age hardened by heating to a temperature of about 250° C., held at that temperature for about ninety minutes, and then allowed to cool to room temperature.
7. The alloy of claim 2 , wherein the alloy has a tensile strength value of about 470 to 515 N/mm 2 .
8. The alloy of claim 2 , wherein the alloy has a yield strength value of about 345 to 365 N/mm 2 .
9. The alloy of claim 2 , wherein the alloy has an elongation value of about 22 to 25 A %.
10. The alloy of claim 2 , wherein the alloy has a grain size of about 880 to 930 μm.