Polymer additive layer manufacturing
An additive layer manufacturing method for producing a shaped article, comprising providing a powdered thermoplastic polymer material ( 7, 8 ) having a re-solidification temperature at most 10% below its melting temperature on the Celsius scale, depositing successive layers of the powdered polymer material ( 7, 8 ) and selectively sintering each layer prior to deposition of the subsequent layer so as to form the article, wherein during its production the article is maintained at a temperature above the glass transition temperature and significantly below the re-solidification temperature of the polymer.
1. An additive layer manufacturing (ALM) method for producing a shaped article, comprising providing a powdered thermoplastic polymer material selected from the group comprising polyaryletherketones, polyetheretherketones (PEEK), or polyetherketones (PEK) having a re-solidification temperature at most 10% below its melting temperature on the Celsius scale, depositing successive layers of the powdered polymer material and selectively sintering each layer prior to deposition of the subsequent layer so as to form a support structure and then form the article upon the support structure, the support structure and the article are produced using the same ALM method, wherein during its production the article is maintained at a temperature above the glass transition temperature and below the re-solidification temperature of the polymer, and the shaped article is constructed within a sintering chamber maintained at a temperature below the continuous service temperature of the polymer material.
2. A method according to claim 1 , wherein the polymer is a semi-crystalline polymer.
3. A method according to claim 1 , wherein the polymer has a re-solidification temperature at most 5% below its melting temperature on the Celsius scale.
4. A method according to claim 1 , wherein the shaped article is constructed on a horizontal, planar substrate.
5. A method according to claim 4 , wherein the substrate is moveable in the vertical direction.
6. A method according to claim 1 , wherein the sintering chamber is maintained at a temperature above the glass transition temperature and significantly below the re-solidification temperature of the polymer.
7. A method according to claim 1 , wherein the sintering chamber is maintained at a temperature below the temperature at which the strength of the polymer material after 2,000 hours at that temperature is decreased by at least 10% due to thermal aging.
8. A method according to claim 1 , wherein the un-sintered polymer material is re-used for producing another article according to the method of claim 1 .
9. A method according to claim 1 , wherein the polymer is selectively sintered using a laser source.
10. A method according to claim 1 , wherein the support structure includes an array of slender struts.
11. An additive layer manufacturing (ALM) method for producing a shaped article, comprising providing a powdered thermoplastic polymer material having a re-solidification temperature not significantly below its melting temperature on the Celsius scale, depositing successive layers of the powdered polymer material and selectively sintering each layer prior to deposition of the subsequent layer so as to produce a support structure and then form the article upon the support structure, the support structure and the article are produced using the same ALM method, wherein during its production the article is maintained at a temperature above the glass transition temperature and below the re-solidification temperature of the polymer, and the shaped article is constructed within a sintering chamber maintained at a temperature below the continuous service temperature of the polymer material.
12. An additive layer manufacturing (ALM) method for producing a shaped article, comprising providing a powdered thermoplastic polymer material, depositing successive layers of the powdered polymer material and selectively sintering each layer prior to deposition of the subsequent layer so as to produce a support structure and then form the article upon the support structure, the support structure and the article are produced using the same ALM method, wherein during its production the article is maintained at a temperature above the glass transition temperature and below the re-solidification temperature of the polymer, and wherein the polymer is selected from the group comprising polyaryletherketones, polyetheretherketones (PEEK), or polyetherketones (PEK), and the shaped article is constructed within a sintering chamber maintained at a temperature below the continuous service temperature of the polymer material.
13. An additive layer manufacturing (ALM) method for producing a shaped article, comprising providing a powdered thermoplastic polymer material, depositing successive layers of the powdered polymer material and selectively sintering each layer prior to deposition of the subsequent layer so as to produce a support structure and then form the article upon the support structure, the support structure and the article are produced using the same ALM method, wherein during its production the article is maintained at a temperature above the glass transition temperature and significantly below the re-solidification temperature of the polymer, and wherein the polymer has a continuous service temperature in excess of 100 degrees Celsius, and the shaped article is constructed within a sintering chamber maintained at a temperature below the continuous service temperature of the polymer material.