Polyester resins
A polyester AB is disclosed comprising moieties derived from di- or polyfunctional organic acid compounds A and moieties derived from di- or polyfunctional organic hydroxy compounds B, wherein the compounds A comprise “hard” acid compounds Al selected from the group consisting of isophthalic acid, trimellithic acid anhydride, hexahydrophthalic acid, cyclohexane-1,4-dicarboxylic acid, and tetrahydrophthalic acid, and soft acid compounds A2 selected from the group consisting of adipic acid, dimer fatty acids, and sebacic acid, and the compounds B comprise “hard” hydroxyfunctional compounds selected from the group consisting of trimethylolpropane, 1,2-bishydroxymethyl cyclohexane, and 1,2-dihydroxy-propane, and soft hydroxyfunctional compounds B2 selected from the group consisting of 1,4-butanediol, 1,6-hexanediol, 2,2′-dihydroxydiethyl ether, and 1,2-bis(2-hydroxypropoxy)-propane, and coating compositions prepared from this polyester together with crosslinkers selected from the group consisting of isocyanates, capped isocyanates, aminoplast crosslinkers, and phenoplast crosslinkers, as well as their application in coating of metal substrates.
1. A polyester AB consisting of moieties derived from di-or polyfunctional organic acid compounds A and moieties derived from di- or polyfunctional organic hydroxy compounds B, wherein A consists of an amount of substance-fraction a 1 of from 0.2 to 0.8 of at least two acid compounds A1, and an amount of substance-fraction a 2 of from 0.2 to 0.8 of at least two acid compounds A2, and wherein the compounds B consist of an amount of substance-fraction b 1 of from 0.05 to 0.8 of at least one hydroxy functional compound B1, and an amount of substance-fraction b 2 of from 0.2 to 0.95 of at least one hydroxy functional compound B2, wherein the sum of the amount of substance fractions a 1 and a 2 is 1, and the sum of the amount of substance fractions b 1 and b 2 is 1, and wherein:
A1 are independently selected from the group consisting of isophthalic acid, trimellithic acid anhydride, hexahydrophthalic acid, cyclohexane-1,4-dicarboxylic acid, and tetrahydrophthalic acid, and
A2 are independently selected from the group consisting of adipic acid, dimer fatty acids, and sebacic acid,
and
B1 are independently selected from the group consisting of trimethylolpropane, 1,2-bishydroxymethyl cyclohexane, and 1,2-dihydroxy-propane, and
B2 are selected from the group consisting of 1,4-butanediol, 1,6-hexanediol, 2,2′-dihydroxydiethyl ether, and 1,2-bis(2-hydroxypropoxy)propane.
2. The polyester AB of claim 1 wherein the ratio of b 1 to b 2 is from 0.05:0.95 to 2:1.
3. The polyester AB of claim 1 wherein the ratio of b 1 to b 2 is from 0.06 to 1.5.
4. The polyester AB of claim 1 wherein two compounds according to A2 are present.
5. The polyester AB of claim 1 wherein at least two compounds according to B1 are present.
6. The polyester AB of claim 2 wherein at least two compounds according to B2 are present.
7. The polyester AB of claim 2 wherein two compounds according to A1, referred to as A11 and A12 are present.
8. The polyester AB of claim 7 wherein the two compounds A11 and A12 are present in a molar ratio of from 3 mol : 1 mol to 1 mol : 3 mol.
9. The polyester AB of claim 1 wherein two compounds according to B1, referred to as B11 and B12 are present.
10. The polyester AB of claim 9 wherein the two compounds B11 and B12 are present in a molar ratio of from 3 mol : 1 mol to 1 mol : 3 mol.
11. A method of use of the polyester AB of claim 1 for manufacturing coatings, comprising the steps of
admixing to the said polyester AB a phenolic resin C in a range of mass ratios of m(AB):m(C) of from 50:95 to 50:5 to provide a mixture,
applying the mixture to a metal surface by spraying, dipping, brushing, blade coating, or roller coating, and
curing the coated substrate at a temperature of from 100° C. to 250° C.