Purification systems and methods
A method of preparing hydrogel particles includes applying a solution including a plurality of hydrogel particles to a stir cell. A retentate side of a filter defines a lower surface of the stir cell. The filter has the retentate side and a permeate side. The method further includes, while stirring the solution within the stir cell, dispensing a buffer solution at a first flow rate to the stir cell and drawing a permeate from the permeate side of the filter using a pump at a second flow rate, the permeate including a subset of the plurality of hydrogel particles.
1. A method of preparing hydrogel polymeric particles, the method comprising:
filtering a plurality of hydrogel polymeric particles through a first filter having a pore size at a first permeate velocity to provide a first subset of hydrogel polymeric particles in the permeate and having a first particle size distribution; and
filtering the first subset of hydrogel polymeric particles through a second filter having the pore size at a second permeate velocity to provide a second subset of hydrogel polymeric particles in the retentate derived from the first subset of hydrogel polymeric particles and having a second particle size distribution narrower than the first particle size distribution;
wherein the average particle size of the second subset of hydrogel polymeric particles is in a range of 0.3 micrometers to 1.5 micrometers;
wherein the first and second permeate velocities are different.
2. The method of claim 1 , wherein the first permeate velocity is greater than the second permeate velocity.
3. The method of claim 1 , wherein the first permeate velocity is in a range of 0.01 cm/min to 0.17 cm/min, a range of 0.02 cm/min to 0.17 cm/min, a range of 0.05 cm/min to 0.16 cm/min, a range of 0.07 to 0.15 cm/min, or a range of 0.08 cm/min to 0.15 cm/min.
4. The method of claim 1 , wherein the second permeate velocity is in a range of 0.01 cm/min to 0.17 cm/min, a range of 0.02 cm/min to 0.14 cm/min, a range of 0.02 cm/min to 0.11 cm/min, a range of 0.02 cm/min to 0.085 cm/min, or a range of 0.02 cm/min to 0.075 cm/min.
5. A method of preparing polymeric particles, the method comprising:
filtering a plurality of polymeric particles through a first filter having a first pore size at a first permeate velocity to provide a first subset of polymeric particles having a first average particle size; and
filtering the first subset of polymeric particles through a second filter having a second pore size at a second permeate velocity to provide a second subset of polymeric particles having a second average particle size greater than the first average particle size;
wherein the second average particle size is in a range of 0.3 micrometers to 1.5 micrometers;
wherein the first and second pore sizes are at least the second average particle size; and
wherein the first and second pore sizes are approximately equal.
6. The method of claim 5 , wherein the first permeate velocity is greater than the second permeate velocity.
7. The method of claim 5 , wherein the first permeate velocity is in a range of 0.01 cm/min to 0.17 cm/min, a range of 0.02 cm/min to 0.17 cm/min, a range of 0.05 cm/min to 0.16 cm/min, a range of 0.07 to 0.15 cm/min, or a range of 0.08 cm/min to 0.15 cm/min.
8. The method of claim 5 , wherein the second permeate velocity is in a range of 0.01 cm/min to 0.17 cm/min, a range of 0.02 cm/min to 0.14 cm/min, a range of 0.02 cm/min to 0.11 cm/min, a range of 0.02 cm/min to 0.085 cm/min, or a range of 0.02 cm/min to 0.075 cm/min.
9. The method of claim 7 , wherein the plurality of polymeric particles are hydrogel particles.