Impeller brazing method
The present invention relates to an impeller manufacturing method in which a thermal cycle is performed on an assembly body with a brazing material formed of a Ni-containing Au alloy being placed at a bond portion of at least two impeller constituent members. The thermal cycle includes a temperature increasing process with a temperature increasing rate of 20° C./hr. to 100° C./hr., the process including a first intermediate retention and a second intermediate retention each keeping the temperature, the first intermediate retention performed in a temperature range of 500° C. to 850° C. and the second intermediate retention performed in a temperature range of 850° C. to 950° C. (but not including 850° C.). In the thermal cycle, the temperature is increased in a temperature range exceeding 950° C. after the second intermediate retention at a rate lower than that before the second intermediate retention.
1. An impeller manufacturing method comprising performing a thermal cycle for bonding on an assembly body with a brazing material interposed at a bond portion between at least two impeller constituent members, wherein the thermal cycle includes:
a temperature increasing process of increasing a temperature to a retention temperature including a first intermediate retention and a second intermediate retention,
wherein, in the temperature increasing process, a temperature increasing rate is 20° C./hr. to 100° C./hr. during the temperature increasing process, but not during the first intermediate retention and the second intermediate retention,
wherein the first intermediate retention is performed in a temperature range of 500° C. to 850° C.,
wherein the second intermediate retention is performed in a temperature range of 850° C. to 950° C., but not including 850° C.,
wherein, in a temperature range exceeding 950° C. after the second intermediate retention, the temperature is increased at a rate slower than a rate before the second intermediate retention;
a retaining process of retaining at the retention temperature in a temperature range equal to or higher than a melting temperature of the brazing material,
wherein, in the retaining process, the retention temperature is selected from a range of 1000° C. to 1050° C.; and
a temperature decreasing process of decreasing the temperature from the retention temperature to a room temperature,
wherein, in the temperature decreasing process, a retention is performed in a temperature range of 930° C. to 970° C., for 0.5 to 2 hours.
2. The impeller manufacturing method according to claim 1 , wherein
in the temperature decreasing process,
a temperature decreasing rate is 20° C./hr. to 100° C./hr., and
from the retention temperature to 950° C., the temperature is decreased at a rate slower than a temperature decreasing rate at a lower temperature.
3. The impeller manufacturing method according to claim 1 , wherein
the thermal cycle is performed with the assembly body being placed with respect to a first heating body heating the assembly body from an inner circumferential side of the assembly body.
4. The impeller manufacturing method according to claim 3 , wherein
the first heating body is integrally provided together with a second heating body supporting the assembly body from below in a vertical direction.
5. The impeller manufacturing method according to claim 3 , wherein
the first heating body satisfies 0.5h 2 ≦h 1 ≦20h 2 ,
where h 1 is a height of the first heating body and h 2 is a height of the assembly body.
6. The impeller manufacturing method according to claim 4 , wherein
the first heating body satisfies 0.5h 2 ≦h 1 ≦20h 2 ,
where h 1 is a height of the first heating body and h 2 is a height of the assembly body.
7. The impeller manufacturing method according to claim 1 , wherein, in the temperature decreasing process, the retention is performed at a temperature of approximately 950° C.