Methods to recover cesium formate from a mixed alkali metal formate blend
View Patent ↗Methods to recover or separate cesium formate or rubidium formate or both from a mixed alkali metal formate blend are described. One method involves adding cesium sulfate or rubidium sulfate to the mixed alkali metal formate blend in order to preferentially precipitate potassium sulfate from the mixed alkali metal formate blend. Another method involves adding cesium carbonate or cesium bicarbonate or both to preferentially precipitate potassium carbonate/bicarbonate and/or other non-cesium or non-rubidium metals from the mixed alkali metal blend. Further optional steps are also described. Still one other method involves converting cesium sulfate to cesium hydroxide.
1. A method to convert at least a portion of cesium sulfate in solution to cesium hydroxide in said solution, said method comprising adding potassium hydroxide to said solution to form potassium sulfate precipitate and cesium hydroxide in said solution; and
separating at least a portion of said potassium sulfate precipitate from said solution to obtain a resulting solution containing cesium hydroxide.
2. The method of claim 1 , further comprising a) reducing water content from said resulting solution in order to precipitate additional potassium sulfate and b) separating at least a portion of said additional potassium sulfate precipitate from said resulting solution, and optionally repeating a) and b) one or more times.
3. The method of claim 2 , wherein said removing water is achieved by heating said resulting solution.
4. The method of claim 2 , wherein said repeating of a) and b) occurs at least once and said removing water is achieved by heating.
5. The method of claim 1 , wherein said solution containing said cesium sulfate is at a temperature or raised to a temperature of about 50° C. or higher, so as to preferentially precipitate potassium sulfate and form cesium hydroxide in said solution.
6. The method of claim 1 , further comprising a) heating said resulting solution to a temperature of from about 50° C. to boiling point of said resulting solution in order to reduce water content and precipitate additional potassium sulfate and b) separating at least a portion of additional potassium sulfate precipitate from said resulting solution, and repeating a) and b) at least once.
7. The method of claim 1 , wherein said cesium sulfate in solution comprises from about 1 wt % to about 100 wt % cesium sulfate based on the weight of alkali metal salts present in said solution.
8. The method of claim 1 , wherein said cesium sulfate in solution comprises from about 60 wt % to about 99 wt % cesium sulfate based on the weight of alkali metal salts present in said solution.
9. The method of claim 1 , wherein said cesium sulfate in solution comprises from about 90 wt % to about 99 wt % cesium sulfate based on the weight of alkali metal salts present in said solution.
10. The method of claim 1 , wherein said potassium hydroxide is added in an amount to react with from about 10 wt % to 100 wt % of cesium sulfate present in said solution.
11. The method of claim 1 , wherein said potassium hydroxide is added in an amount to react with from 80 wt % to 99.5 wt % of cesium sulfate in said solution.
12. The method of claim 1 , wherein said potassium hydroxide is added in an amount to react with from 95 wt % to 99 wt % of cesium sulfate in said solution.
13. The method of claim 1 , wherein said potassium hydroxide is added as one addition to said solution.
14. The method of claim 1 , wherein said potassium hydroxide is added as multiple additions at separate times to said solution.
15. The method of claim 1 , wherein said adding is continuous, semi-continuous, or by single addition prior to said separating.
16. A method to convert at least a portion of cesium sulfate or rubidium sulfate or both in solution to cesium hydroxide or rubidium hydroxide or both in said solution, said method comprising adding potassium hydroxide to said solution to form potassium sulfate precipitate and cesium hydroxide or rubidium hydroxide or both in said solution; and
separating at least a portion of said potassium sulfate precipitate from said solution to obtain a resulting solution containing cesium hydroxide or rubidium hydroxide or both.
17. The method of claim 16 , further comprising a) reducing water content from said resulting solution in order to precipitate additional potassium sulfate and b) separating at least a portion of said additional potassium sulfate precipitate from said resulting solution, and optionally repeating a) and b) one or more times.
18. The method of claim 1 , wherein said method is conducted in the absence of a barium compound.
19. The method of claim 2 , wherein said method is conducted in the absence of a barium compound.
20. The method of claim 16 , wherein said method is conducted in the absence of a barium compound.
21. The method of claim 17 , wherein said method is conducted in the absence of a barium compound.