Coating layer for anti-glare film and anti-glare film comprising the same
The present invention relates to a coating layer for an anti-glare film that can prevent glaring by reflection of external light on a surface of a display and an anti-glare film comprising the same. The coating layer for an anti-glare film according to an exemplary embodiment of the present invention comprises a binder resin, organic particulates, and inorganic particulates, and differences differences between refractive indexes of the binder resin and the organic particulates and between refractive indexes of the binder resin and inorganic particulates are each 0.3 or less. The coating layer for an anti-glare film according to an exemplary embodiment of the present invention can provide an anti-glare film having excellent anti-glare property, distinctness-of-image, and contrast, such that the coating layer can be applied to a display having high resolution, and has excellent scratch resistance in terms of a coating thickness of a thin film, such that it is easy to enlarge a polarizing plate.
1. A coating layer for an anti-glare film, comprising:
a binder resin,
organic particulates, one or more selected from polystyrene, polymethylmethacrylate, polymethylacrylate, polyacrylate, polyacrylate-co-styrene, polymethylacrylate-co-styrene, polymethylmethacrylate-co-styrene, polycarbonate, polyvinyl chloride, polybutyleneterephthalate, polyethyleneterephthalate, polyamides, polyimides, polysulfone, polyphenylene oxide, polyacetal, epoxy resin, phenol resin, silicon resin, melamine resin, benzoguamine, polydivinylbenzene, polydivinylbenzene-co-styrene, polydivinylbenzene-co-acrylate, polydiallylphthalate and triallylisocyanurate polymer, or two or more copolymers thereof, and
inorganic particulates, one or more selected from the group consisting of silica, silicon particle, aluminum hydroxide, magnesium hydroxide, alumina, zirconia and titania,
wherein differences between refractive indexes of the binder resin and the organic particulates and between refractive indexes of the binder resin and inorganic particulates are each 0.3 or less,
wherein the organic particulate has a spherical shape, and a particle diameter is in the range of 1 to 3.5 μm,
wherein the inorganic particulate has a spherical shape, and a particle diameter is in the range of 4 to 10 μm, wherein the content of the inorganic particulates is in the range of 20 to 80 parts by weight on the basis of 100 parts by weight of the organic particulates, and
wherein a thickness of the coating layer for the anti-glare film is in the range of 1 to 4 μm, and the organic particulates and the inorganic particulates form a single particle layer without overlapping of the organic and the inorganic particulates.
2. The coating layer for an anti-glare film according to claim 1 , wherein the total content of the organic particulates and the inorganic particulates is in the range of 1 to 30 parts by weight on the basis of 100 parts by weight of the binder resin.
3. The coating layer for an anti-glare film according to claim 1 , wherein the binder resin is an acryl-based binder resin.
4. The coating layer for an anti-glare film according to claim 3 , wherein the acryl-based binder resin comprises one or more selected from the group consisting of an acrylate monomer and an acrylate oligomer.
5. An anti-glare film comprising the coating layer for the anti-glare film according to claim 1 .