Zn—Mg alloy plated steel sheet, and method for manufacturing same
Provided are a Zn—Mg alloy plated steel sheet and a method for manufacturing same. The Zn—Mg alloy plated steel sheet comprises a base steel sheet and a Zn—Mg plating layer formed on the base steel sheet, wherein the content of Mg in the Zn—Mg plating layer is 8 weight % or less (provided that 0 weight % is excluded), and the Zn—Mg plating layer is a compound phase of Zn and Mg2Zn11. According to the present invention, provided are a Zn—Mg alloy plated steel sheet and a method for manufacturing the same, wherein the Zn—Mg alloy plated steel sheet has excellent corrosion resistance, high adhesion, and superior surface quality of metallic luster.
1. A zinc (Zn)-magnesium (Mg) alloy-plated steel sheet, comprising:
a base steel sheet; and
a Zn—Mg plating layer formed on the base steel sheet,
wherein an Mg content of the Zn—Mg plating layer is 8 wt % or less and higher than 0 wt %,
the Zn—Mg plating layer is a complex phase of Zn and Mg 2 Zn 11 , and
an average size of surface grains of the Zn—Mg alloy-plated steel sheet is 90 μm or less and higher than 0 μm.
2. The zinc (Zn)-magnesium (Mg) alloy-plated steel sheet of claim 1 , wherein a phase ratio of Zn to Mg 2 Zn 11 is 1:1 to 1:3 in the complex phase.
3. The zinc (Zn)-magnesium (Mg) alloy-plated steel sheet of claim 1 , wherein a thickness of the Zn—Mg plating layer is 1 μm to 3 μm.
4. The zinc (Zn)-magnesium (Mg) alloy-plated steel sheet of claim 1 , wherein the base steel sheet is a cold-rolled steel sheet or a hot-rolled steel sheet.
5. The zinc (Zn)-magnesium (Mg) alloy-plated steel sheet of claim 1 , wherein an Mg content of the Zn—Mg plating layer is 6.3 wt % or less (but above 0 wt %).