Method of manufacturing negative electrode for solid-state battery, method of manufacturing solid-state battery, and negative electrode slurry
Provided is a method of manufacturing a negative electrode for a solid-state battery, the method including: a step of mixing a negative electrode active material, a sulfide solid electrolyte, a binder, and a solvent with each other to prepare a negative electrode slurry; a step of applying the prepared negative electrode slurry to a surface of a solid electrolyte layer of the solid-state battery or a substrate of the negative electrode; and a step of drying the applied negative electrode slurry. In this method, the solvent is butyl butyrate, and the binder is a copolymer containing a vinylidene fluoride (VDF) monomer unit and a hexafluoropropylene (HFP) monomer unit, in which a molar ratio of the HFP monomer unit to a total amount of the VDF monomer unit and the HFP monomer unit is 10% to 25%.
1. A method of manufacturing a negative electrode for a solid-state battery, the method comprising:
a first step of mixing a negative electrode active material, a sulfide solid electrolyte, a copolymer as a binder, and butyl butyrate as a solvent with each other to prepare a negative electrode slurry, in which the copolymer consists of a vinylidene fluoride monomer unit and a hexafluoropropylene monomer unit, and a molar ratio of the hexafluoropropylene monomer unit to a total amount of the vinylidene fluoride monomer unit and the hexafluoropropylene monomer unit is 10% to 25%, wherein the first step includes:
a step of adding the binder to the solvent and then leaving the binder to stand in the solvent such that the binder is swollen, and
a step of dispersing the swollen binder in the solvent;
a second step of applying the prepared negative electrode slurry to a surface of a solid electrolyte layer of the solid-state battery or a substrate of the negative electrode; and
a third step of drying the applied negative electrode slurry.
2. The method according to claim 1 , wherein
the binder is added to the solvent and then is left to stand in the solvent until the binder is in a transparent state.
3. The method according to claim 1 , wherein
in the first step, a content of the binder is 0.5 parts by mass to 3.5 parts by mass with respect to 100 parts by mass of the negative electrode active material.
4. A method of manufacturing a solid-state battery, the method comprising:
a step of laminating a negative electrode for a solid-state battery which is obtained using the method according to claim 1 , a solid electrolyte layer containing a solid electrolyte, and a positive electrode containing a positive electrode active material.
5. The method according to claim 1 , wherein in the first step, the binder is left to stand in the solvent for 2 hours or more such that the binder is swollen.