Polyurethane adhesives for reverse osmosis modules
An adhesive composition suitable for reverse osmosis modules, the adhesive composition includes (I) a polyurethane composition that includes (A) an isocyanate group-containing pre-polymer comprising a reaction product of (i) castor oil or a derivative thereof; and (ii) a polyisocyanate; and (iii) optionally a second polyol; and (B) an isocyanate-reactive polyol mixture comprising: (i) a polybutadiene polyol; and (ii) a urethane catalyst; and (iii) optionally the second polyol; and (II) a plasticizer wherein the adhesive composition is essentially free from diluent oils and solvents.
1. An adhesive composition suitable for reverse osmosis modules, the adhesive composition comprising:
(I) from 65 wt. % to 99 wt. % of a polyurethane composition based on a total wt. % of the adhesive composition, the polyurethane composition comprising:
(A) an isocyanate group-containing pre-polymer comprising a reaction product of (i) castor oil or a derivative thereof; and (ii) a polyisocyanate; and (iii) optionally a second polyol; and
(B) an isocyanate-reactive polyol mixture comprising: (i) a polybutadiene polyol; and (ii) a urethane catalyst; and (iii) optionally the second polyol; and
(II) from 1 wt. % to about 35 wt. % of a plasticizer based on the total wt. % of the adhesive composition,
wherein the adhesive composition is essentially free from diluent oils and solvents;
wherein the viscosity of part (B) is at least 1,000 cps; and
wherein the adhesive composition has a Shore hardness of greater than 20 A when fully cured.
2. The adhesive composition according to claim 1 , wherein an initial mix viscosity of the adhesive composition, defined as the viscosity when parts (I)(A), (I)(B), and (II) are mixed together, is at least 10,000 cps.
3. The adhesive composition according to claim 2 , wherein the initial mix viscosity of the adhesive composition is between about 10,000 cps and about 40,000 cps.
4. The adhesive composition according to claim 1 , wherein the Shore hardness is between 60 A and 80 D when fully cured.
5. The adhesive composition according to claim 1 , wherein the Shore hardness is at least 35 D when fully cured.
6. The adhesive composition according to claim 1 , wherein the Shore hardness is between 35 D and 80 D when fully cured.
7. The adhesive composition according to claim 1 , wherein the adhesive composition has a tensile strength greater than 100 psi when fully cured.
8. The adhesive composition according to claim 7 , wherein the tensile strength of the adhesive composition is at least 1,000 psi when fully cured.
9. The adhesive composition according to claim 8 , wherein the tensile strength of the adhesive composition is at least 2,000 psi when fully cured.
10. The adhesive composition according to claim 1 , wherein either part (A) or part (B) comprises at least 4 wt. % of the second polyol based on a total weight percent of part (A) and part (B).
11. The adhesive composition according to claim 10 , wherein the second polyol is chosen from a group of polyols having a molecular weight less than about 600.
12. The adhesive composition according to claim 11 , wherein the second polyol is a polyol having a molecular weight between 80-300 Daltons.
13. The adhesive composition according to claim 12 , wherein the second polyol is a diol.
14. The adhesive composition according to claim 13 , wherein the second polyol is selected from the group consisting of 2-ethyl-1,3-hexanediol; 1,2-propanediol; 1,3-butanediol; 2,2,4-trimethyl-1,3-pentanediol, 1,12-octadecanediol; 1,2-hexanediol; 1,2-octanediol; and 1,2-decanediol.
15. The adhesive composition according to claim 11 , wherein the second polyol is a polypropylene glycol or a polytetramethylene ether glycol.
16. The adhesive composition according to claim 1 , wherein at least one of part (I)(A) and part (I)(B) further comprise a filler, a thixotropic agent or a combination thereof.
17. The adhesive composition according to claim 16 , wherein at least one of part (I)(A) and part (I)(B) comprise a filler selected from the group consisting of talc, calcium carbonate, barium sulfate, magnesium hydroxide, clay, mica, titanium dioxide, and combinations thereof.
18. The adhesive composition according to claim 16 , wherein part (I)(B) of the adhesive composition further comprises a thixotropic agent.
19. The adhesive composition according to claim 18 , wherein the thixotropic agent is selected from the group consisting of fumed silica, amorphous silicon dioxide, talc, clay and combinations thereof.
20. The adhesive composition according to claim 1 , wherein part (I) of the adhesive composition includes between about 10 wt. % and about 90 wt. % of part (A) based on the total weight of part (I) and between about 10 wt. % and about 90 wt. % of part (B) based on the total weight of part (I).
21. The adhesive composition according to claim 20 , wherein part (I) of the adhesive composition includes about 50 wt. % of part (A) based on the total weight of part (I) and about 50 wt. % of part (B) based on the total weight of part (I).
22. An adhesive composition suitable for reverse osmosis modules, the adhesive composition comprising:
(I) from 65 wt % to 99 wt % of a polyurethane composition, based on a total weight of the adhesive composition, the polyurethane composition comprising:
(A) an isocyanate group-containing pre-polymer comprising a reaction product of (i) castor oil or a derivative thereof; and (ii) a polyisocyanate; and
(B) an isocyanate-reactive polyol mixture comprising: (i) polybutadiene polyol; (ii) a urethane catalyst; and (iii) a secondary polyol; wherein the viscosity of part (B) is at least 1,000 cps; and
(II) from 1 wt. % to 35 wt. % of a plasticizer, based on the total wt. % of the adhesive composition,
wherein the adhesive composition is essentially free from diluents oils and solvents;
wherein a tensile strength of the adhesive composition when fully cured is at least 1,000 psi; and
wherein a Shore hardness of the adhesive composition when fully cured is between about 35 D and about 75 D.
23. The adhesive composition according to claim 22 , wherein the plasticizer is selected from the group consisting of azelates, sebacates, maleates, succinates, phthalates, adipates, dicarboxylic/tricarboxylic ester-based plasticizers, phosphates, trimellitates, glutarates, citrates, dipropylene glycol dibenzoates, diethylene glycol dibenzoates, epoxidized soybean oil, esters of soybean oil, and combinations thereof.
24. The adhesive composition according to claim 23 , wherein the plasticizer is selected from the group consisting of dipropylene glycol dibenzoates, diethylene glycol dibenzoates, epoxidized soybean oil, esters of soybean oil, diheptyl adipate, dioctyl adipate, dinonyl adipate, and combinations thereof.
25. A reverse osmosis module comprising an adhesive composition according to claim 1 .
26. A reverse osmosis module comprising
an adhesive composition according to claim 22 .