Magnesium phosphate cement
Magnesium phosphate cement binder systems and method for providing magnesium phosphate cements are described. In an embodiment, a magnesium phosphate cement binder system may include magnesium oxide that has been calcined at a temperature of between about 900° F. to about 1800° F. The magnesium phosphate cement binder system may also include a phosphate material. Other formulations, compositions, and methods are also described.
1. A method of making a magnesium phosphate cement comprising:
providing magnesium oxide calcined to exhibit a caustic magnesia activity neutralization time of between about 9 seconds to about 30 seconds using a 1.0N acetic acid and a magnesium oxide content of between about 10% to about 100%;
providing a phosphate material;
combining the magnesium oxide and the phosphate material; and
hydrating the combined magnesium oxide and phosphate material.
2. The method of making a magnesium phosphate cement of claim 1 , wherein the magnesium oxide is calcined using a multiple hearth furnace.
3. The method of making a magnesium phosphate cement of claim 2 , wherein the multiple hearth furnace includes a Herreshoff multiple hearth furnace.
4. The method of making a magnesium phosphate cement of claim 1 , wherein the magnesium oxide is calcined using a multiple hearth furnace, and includes a surface area in the range of between about 10 m 2 /g to about 120 m 2 /g.
5. The method of making a magnesium phosphate cement of claim 1 , wherein combining the magnesium oxide and the phosphate material includes combining the magnesium oxide in a weight ratio to the phosphate material of between about 1:5 to about 5:1.
6. The method of making a magnesium phosphate cement of claim 1 , wherein hydrating the combined magnesium oxide and phosphate material includes hydrating with chilled hydration water having a temperature between about 33° F. to about 70° F.
7. The method of making a magnesium phosphate cement of claim 1 , further including carbonating hydration water used to hydrate the combined magnesium and phosphate material.
8. The method of making a magnesium phosphate cement of claim 1 , further including combining the magnesium oxide and phosphate material with a powdered carbonate.
9. The method of making a magnesium phosphate cement of claim 1 , wherein providing the magnesium oxide includes treating a surface of the magnesium oxide to increase the time for the binder system to reach a maximum heat of hydration in response to hydrating the combined magnesium oxide and phosphate material.
10. The method of making a magnesium phosphate cement of claim 9 , wherein treating the surface of the magnesium oxide includes treating the surface of the magnesium oxide with one or more of a hydrocarbon oil, a hydrocarbon wax, an organic glycol, a surfactant, a siliconized oil, a siliconized wax, a siliconized glycol, a fluorinated fluid, a monomer, an oligomer, a polymer, a reactive silane coupling agent, a fatty acid, a fatty acid ester, a polysaccharide, a long chain alkyl silicone monomer, a time releasing water soluble polymer, a time releasing water soluble oligomer, a gelatin, an acetate, and a borate.
11. The method of making a magnesium phosphate cement of claim 1 , wherein providing the magnesium oxide includes reacting the magnesium oxide with sulfuric acid to increase surface reactivity of the magnesium oxide.
12. The method of making a magnesium phosphate cement of claim 1 , further including combining the magnesium oxide and the phosphate material with a cure retardant including one or more of zinc oxide, lithium citrate, lithium acetate, lignosulfonates, zeolites, polysaccharides, amino acids, tetraborates, and organic acid salts.
13. The method of making a magnesium phosphate cement of claim 1 , wherein the phosphate material includes one or more of an organic phosphate salt and an inorganic phosphate salt.
14. The method of making a magnesium phosphate cement of claim 13 , wherein the phosphate material includes one or more of a mono-potassium phosphate, a dihydrogen phosphate, a phosphonate, polyphosphate, pyrophosphate, a phosphoric acid, and an orthophosphate.
15. The method of making a magnesium phosphate cement of claim 1 , further comprising:
applying a layer of the hydrated combined magnesium oxide and phosphate material to at least one surface of a construction board.
16. The method of making a magnesium phosphate cement of claim 15 , wherein the layer of hydrated combined magnesium oxide and phosphate material has a thickness of between about 1/64 inch to about 1 inch.
17. The method of making a magnesium phosphate cement of claim 15 , wherein applying the layer of the hydrated combined magnesium oxide and phosphate material to the at least one surface of the construction board includes one or more of spray coating, wet shotcrete coating, dry shotcrete coating, roller coating, curtain coating, and powder coating.
18. The method of making a magnesium phosphate cement of claim 15 , wherein the construction board includes construction board based upon one or more of gypsum, stucco, plaster, wood, Styrofoam, Portland cement, structural insulated panel, wood fiber, and composite panel.
19. The method of making a magnesium phosphate cement of claim 15 , wherein the construction board includes one or more of wall board, floor board, ceiling panel, roofing panel, roofing membrane, furniture veneer, door, door frame, window frame, and flooring material.