Method for manufacturing microwavable food containers
Methods and apparatus for manufacturing vacuum forming a produce container using a fiber-based slurry. The slurry includes a moisture barrier comprising alkylketene dimer in the range of about 4% by weight, and a cationic liquid starch component in the range of 1%-7% by weight.
1. A method of manufacturing a microwavable food container comprising the steps of:
preparing a fiber-based slurry mixture including: i) a moisture barrier component comprising alkyl ketene dimer (AKD); ii) an oil barrier component comprising a water based emulsion of fluorine containing at least one of a fluorocarbon resin and a fluorine polymer; and iii) a rigidity component comprising liquid starch in the range of 1%-5% by weight;
forming a wire mesh over a mold comprising a mirror image of the microwavable food container;
immersing the wire mesh into the fiber-based slurry mixture;
drawing a vacuum across the wire mesh to cause fiber particles to accumulate at the wire mesh surface;
removing the wire mesh including the accumulated fiber particles in the form of the microwavable food container from the slurry mixture;
at least partially drying the microwavable food container; and
applying a vapor barrier to a surface of the at least partially dried microwavable food container, wherein the vapor barrier is different than the oil barrier component.
2. The method of claim 1 , wherein the slurry further comprises a retention aid.
3. The method of claim 2 , wherein the retention aid comprises an organic compound in the range of 0.1-1% of the slurry volume.
4. The method of claim 1 , wherein:
the moisture barrier comprises in the range of 0.5%-10% of the slurry weight; and
the oil barrier comprises in the range of 0.5%-10% of the slurry weight.
5. The method of claim 1 , wherein the moisture barrier is in the range of about 1.5%-4%, the oil barrier is in the range of about 1%-4%, and the retention aid is in the range of about 0.1%-0.5%.
6. The method of claim 1 , wherein the moisture barrier comprises alkyl ketene dimer (AKD) in the range of about 3.5%.
7. The method of claim 1 , further comprising the step of grinding fibers to achieve a freeness in the range of 100-700, and introducing the ground fibers into the slurry.
8. The method of claim 1 , wherein the vapor barrier comprises a long chain fluorine-based polymer.
9. The method of claim 1 , wherein the vapor barrier comprises a spray coating in the range of about 0.1-3% of the slurry weight.
10. A method of manufacturing a microwavable food container, comprising:
preparing a fiber-based slurry mixture including: i) a moisture barrier component in the range of about 1.5%-4% by weight; ii) an oil barrier component in the range of about 1-4% by weight; and iii) a retention aid in the range of about 0.1-0.5% by weight;
immersing a wire mesh mold in the fiber-based slurry mixture;
drawing a vacuum across the wire mesh mold to cause fiber particles to accumulate at the wire mesh surface;
subsequently drying and removing the food container from the mold; and
coating at least one of an inside and outside surface of the food container with a vapor barrier that is different than the oil barrier component.
11. The method of claim 10 , wherein the slurry comprises at least one of: softwood (SW); bagasse; bamboo; old corrugated containers (OCC); and newsprint (NP).
12. The method of claim 11 , wherein the fiber base of the slurry comprises old corrugated containers (OCC) in the range of about 70% and newsprint (NP) in the range of about 30%.