Pressure-sensitive hot melt adhesive compositions
The present invention is related to pressure-sensitive hot melt adhesive compositions and their applications. In particular, the adhesive compositions described herein comprise a block copolymer component, a hydrocarbon tackifier resin component, and a propylene-based polymer component.
1. A pressure-sensitive hot melt adhesive composition consisting essentially of:
from about 30 to about 60 wt % of at least one styrenic block copolymer component;
from about 5 to about 50 wt % of at least one hydrocarbon resin tackifier component;
at least one process oil component; and
from about 5 to about 25 wt % of at least one propylene-based polymer component consisting of about 60 to about 98 wt % propylene and from about 2 to about 40 wt % ethylene and/or C 4 -C 10 alpha-olefins, and wherein the propylene-based polymer component has a melting point less than or equal to about 130° C. and a triad tacticity greater than about 75%;
wherein the pressure-sensitive hot melt adhesive composition has an initial 180° peel strength on steel of less than or equal to about 10 N/25 mm at a coating weight of about 20 gsm; and
wherein the styrenic block copolymer component is a styrene-isoprene block copolymer.
2. The adhesive composition of claim 1 , wherein the propylene-based polymer component consists of about 75 to about 98 wt % propylene and from about 2 to about 25 wt % ethylene and/or C 4 -C 10 alpha-olefins, and wherein the propylene-based polymer component has a melting point less than or equal to about 105° C.
3. The adhesive composition of claim 1 , wherein the tackifier component has a ring-and-ball softening point of from about 50 to about 140° C.
4. The adhesive composition of claim 1 , wherein the propylene-based polymer component further has a heat of fusion less than about 45 J/g.
5. The adhesive composition of claim 4 , wherein the at least one block copolymer component is a radial styrene-isoprene block copolymer.
6. The adhesive composition of claim 1 , wherein the propylene-based polymer component further has an MFR of from about 1 to about 900 g/10 min (230° C., 2.16 kg).
7. The adhesive composition of claim 1 , wherein the composition is removable and wherein the composition is substantially free of silicon oils and waxes.
8. An adhesive article comprising:
a. a substrate; and
b. a pressure-sensitive hot melt adhesive composition consisting essentially of:
from about 30 to about 60 wt % of at least one block copolymer component;
from about 5 to about 50 wt % of at least one hydrocarbon resin tackifier component;
at least one process oil component; and
from about 5 to about 25 wt % of at least one propylene-based polymer component consisting of about 60 to about 98 wt % propylene and from about 2 to about 40 wt % ethylene and/or C 4 -C 10 alpha-olefins, and wherein the propylene-based polymer component has a melting point less than or equal to about 130° C. and a triad tacticity greater than about 75;
wherein the pressure-sensitive hot melt adhesive composition has an initial 180° peel strength on steel of less than or equal to about 10 N/25 mm at a coating weight of about 20 gsm; and
wherein the block copolymer component is a styrene-isoprene block copolymer.
9. The article of claim 8 , wherein the adhesive composition is substantially free of silicon oils and waxes.
10. The article of claim 8 , wherein the article is adhesive tape, wherein the initial 180° peel strength of the tape on glass is lower than or equal to 10 N/25 mm at a coating weight of about 20 gsm.
11. The article of claim 8 , wherein the article is adhesive tape, wherein the initial 180° peel strength of the tape on polyethylene film is lower than or equal to 10 N/25 mm at a coating weight of about 20 gsm.
12. The article of claim 8 , wherein the shear at 23° C. on steel (25 mm*25 mm, 1 Kg) is greater than or equal to 10 hours.
13. A pressure-sensitive hot melt adhesive composition consisting essentially of:
from about 30 to about 60 wt % of at least one block copolymer component, wherein the block copolymer component is a radial styrene-isoprene block copolymer;
from about 5 to about 50 wt % of at least one hydrocarbon resin tackifier component; and
from about 5 to about 25 wt % of at least one propylene-based polymer component consisting of about 60 to about 98 wt % propylene and from about 2 to about 40 wt % ethylene and/or C 4 -C 10 alpha-olefins, and wherein the propylene-based polymer component has a melting point less than or equal to about 130° C. and a triad tacticity greater than about 75%; and
wherein the pressure-sensitive hot melt adhesive composition has an initial 180° peel strength on steel of less than or equal to about 10 N/25 mm at a coating weight of about 20 gsm.
14. A pressure-sensitive hot melt adhesive composition consisting essentially of:
from about 30 to about 60 wt % of at least one block copolymer component;
from about 5 to about 50 wt % of at least one hydrocarbon resin tackifier component; and
from about 5 to about 25 wt % of at least one propylene-based polymer component having a heat of fusion less than about 45 J/g, wherein the propylene-based polymer component consists of about 60 to about 98 wt % propylene and from about 2 to about 40 wt % ethylene and/or C4-C10 alpha-olefins, and wherein the propylene-based polymer component has a melting point less than or equal to about 130° C., a triad tacticity greater than about 75% and an MFR of from about 1 to about 900 g/10 min (230° C., 2.16 kg);
wherein the pressure-sensitive hot melt adhesive composition has an initial 180° peel strength on steel of less than or equal to about 10 N/25 mm at a coating weight of about 20 gsm; and
wherein the block copolymer component is a styrene-isoprene block copolymer.
15. A pressure-sensitive hot melt adhesive composition consisting of:
from about 30 to about 60 wt % of at least one styrenic block copolymer component;
from about 5 to about 50 wt % of at least one hydrocarbon resin tackifier component;
at least one process oil component; and
from about 5 to about 25 wt % of at least one propylene-based polymer component consisting of about 60 to about 98 wt % propylene and from about 2 to about 40 wt % ethylene and/or C 4 -C 10 alpha-olefins, and wherein the propylene-based polymer component has a melting point less than or equal to about 130° C. and a triad tacticity greater than about 75%;
wherein the pressure-sensitive hot melt adhesive composition has an initial 180° peel strength on steel of less than or equal to about 10 N/25 mm at a coating weight of about 20 gsm; and
wherein the styrenic block copolymer component is a styrene-isoprene copolymer.
16. An adhesive article comprising:
a. a substrate; and
b. a pressure-sensitive hot melt adhesive composition consisting of:
from about 30 to about 60 wt % of at least one block copolymer component;
from about 5 to about 50 wt % of at least one hydrocarbon resin tackifier component;
at least one process oil component; and
from about 5 to about 25 wt % of at least one propylene-based polymer component consisting of about 60 to about 98 wt % propylene and from about 2 to about 40 wt % ethylene and/or C 4 -C 10 alpha-olefins, and wherein the propylene-based polymer component has a melting point less than or equal to about 130° C. and a triad tacticity greater than about 75;
wherein the pressure-sensitive hot melt adhesive composition has an initial 180° peel strength on steel of less than or equal to about 10 N/25 mm at a coating weight of about 20 gsm; and
wherein the block copolymer component is a styrene-isoprene copolymer.
17. A pressure-sensitive hot melt adhesive composition consisting of:
from about 30 to about 60 wt % of at least one block copolymer component chosen from a radial styrene-isoprene block copolymer and a radial styrene-butadiene block copolymer;
from about 5 to about 50 wt % of at least one hydrocarbon resin tackifier component; and
from about 5 to about 25 wt % of at least one propylene-based polymer component consisting of about 60 to about 98 wt % propylene and from about 2 to about 40 wt % ethylene and/or C 4 -C 10 alpha-olefins, and wherein the propylene-based polymer component has a melting point less than or equal to about 130° C. and a triad tacticity greater than about 75%;
wherein the pressure-sensitive hot melt adhesive composition has an initial 180° peel strength on steel of less than or equal to about 10 N/25 mm at a coating weight of about 20 gsm; and
wherein the block polymer component is a styrene-isoprene copolymer.
18. A pressure-sensitive hot melt adhesive composition consisting of:
from about 30 to about 60 wt % of at least one block copolymer component;
from about 5 to about 50 wt % of at least one hydrocarbon resin tackifier component; and
from about 5 to about 25 wt % of at least one propylene-based polymer component having a heat of fusion less than about 45 J/g;
wherein the pressure-sensitive hot melt adhesive composition has an initial 180° peel strength on steel of less than or equal to about 10 N/25 mm at a coating weight of about 20 gsm; and
wherein the block copolymer component is a styrene-isoprene copolymer.