Flame-retardant imaged nonwoven fabric
A method of forming flame-retardant nonwoven fabrics by hydroentanglement includes providing a precursor web. The precursor web is subjected to hydroentanglement on a three-dimensional image transfer device to create a patterned and imaged fabric. Treatment with a flame-retardant binder enhances the integrity of the fabric, permitting the nonwoven to exhibit desired physical characteristics, including strength, durability, softness, and drapeability. The treated nonwoven may then be dyed by means applicable to conventional wovens.
1. A method of making a flame-retardant nonwoven fabric, comprising;
a. providing a precursor web,
b. providing a three-dimensional image transfer device,
c. hydroentangling said precursor web on said image transfer device to form a patterned and imaged nonwoven fabric, and
d. applying a binder finish to said nonwoven fabric to impart flame-retardant properties, followed by curing of said binder finish, said binder finish comprising a halogenated urethane derivative imparting said flame-retardant properties.
2. A method of making a flame-retardant nonwoven fabric as in claim 1 , wherein:
said precursor web comprise polyester fibers.
3. A method of making a flame-retardant nonwoven fabric as in claim 2 , wherein:
said precursor web comprise flame-retardant polyester fibers.
4. A method of making a flame-retardant nonwoven fabric as in claim 1 , wherein:
said precursor web is hydroentangled on a formainous surface prior to said step of hydroentangling said precursor web on said image transfer device.
5. A method of making a flame-retardant nonwoven fabric as in claim 1 , wherein said halogenated urethane derivative is selected to comprise a halogenated derivative of a polyurethane backbone.
6. A method of making a flame-retardant nonwoven fabric as in claim 1 , wherein the precursor web comprises a carded, randomized staple length fibrous matrix.
7. A method of making a flame-retardant nonwoven fabric as in claim 1 wherein the precursor web comprises fibers selected from the group consisting of polyester fibers, p-aramid fibers, n-aramid fibers, melamine fibers, and modacrylic fibers, and blends thereof.
8. A method of making a flame-retardant nonwoven fabric as in claim 1 , wherein said binder finish further comprises a metallic salt extinguisant.
9. A method of making a flame-retardant nonwoven fabric as in claim 1 , wherein the flame-retardant nonwoven fabric has a basis weight between about 2.0 ounces per square yard and 10.0 ounces per square yard.
10. A method of making a flame-retardant nonwoven fabric as in claim 1 , wherein the flame-retardant nonwoven fabric has a basis weight between about 0.5 ounces per square yard and 6.0 ounces per square yard.
11. A method of manufacturing a flame-retardant nonwoven fabric, comprising:
a. providing a precursor web,
b. providing a three-dimensional image transfer device,
c. hydroentangling said precursor web on said image transfer device to form a patterned and imaged nonwoven fabric,
d. applying a binder finish to said nonwoven fabric to impart flame-retardant properties, followed by curing of said binder finish, said binder finish comprising a halogenated urethane derivative imparting said flame-retardant properties, and
e. dyeing of said nonwoven fabric.
12. A method of making a flame-retardant nonwoven fabric as in claim 11 , wherein:
said nonwoven fabric is dyed by the method selected from the means consisting of jet dyeing, disperse dying, pad dyeing, screen printing, transfer printing, and the combinations thereof.
13. A method of making a flame-retardant nonwoven fabric as in claim 11 , wherein said halogenated urethane derivative is selected to comprise a halogenated derivative of a polyurethane backbone.
14. A method of making a flame-retardant nonwoven fabric as in claim 11 , wherein the precursor web comprises a carded, randomized staple length fibrous matrix.
15. A method of making a flame-retardant nonwoven fabric as in claim 11 , wherein the precursor web comprises fibers selected from the group consisting of polyester fibers, p-aramid fibers, n-aramid fibers, melamine fibers, and modacrylic fibers, and blends thereof.
16. A method of making a flame-retardant nonwoven fabric as in claim 11 , wherein said binder finish further comprises a metallic salt extinguisant.
17. A method of making a flame-retardant nonwoven fabric as in claim 11 , wherein the flame-retardant nonwoven fabric has a basis weight between about 2.0 ounces per square yard and 10.0 ounces per square yard.
18. A method of making a flame-retardant nonwoven fabric as in claim 11 , wherein the flame-retardant nonwoven fabric has a basis weight between about 0.5 ounces per square yard and 6.0 ounces per square yard.