Process for narrowing short-chain branching distribution in two-step ethylene polymerizations and products
View Patent ↗An improved two-step polymerization process wherein ethylene homopolymer is produced in a first reactor and ethylene copolymer having narrowed short-chain branching distribution is prepared in a second reactor. Narrowed short-chain branching distribution of the copolymer is achieved by including specific silane modifiers in the second reactor.
1. In a two-step process wherein ethylene homopolymer is produced in a first polymerization reactor and ethylene-α-olefin copolymer is produced in a second polymerization reactor, said polymerizations conducted in an inert hydrocarbon medium using a solid high activity transition metal-containing catalyst and organoaluminum co-cocatalyst, and said homopolymer and copolymer are combined to obtain a final polyethylene resin product, to narrow the short-chain branching distribution of the ethylene-α-olefin copolymer, the improvement comprising conducting the copolymerization in the second polymerization reactor in the presence of from 1 to 100 ppm, based on the inert hydrocarbon medium, monoalkyltrialkoxysilane of the formula
R 2 Si(OR 3 ) 3
where R 2 is a C 1-10 alkyl group and R 3 is a C 1-5 alkyl group while maintaining reactor conditions and feed rates to produce copolymer having a density of 0.940 g/cm 3 or less and containing 90 percent or more low short-chain branched copolymer having fewer than 10 branches per 1000 carbon atoms.
2. The process of claim 1 wherein reactor conditions and feed rates in the second polymerization reactor are maintained to produce copolymer having a density from 0.915 to 0.940 g/cm 3 and melt index from 0.001 to 10 g/10 min.
3. The process of claim 2 wherein the α-olefin comonomer copolymerized with ethylene in the second polymerization reactor is butene-1, hexene-1 or octene-1.
4. The process of claim 2 wherein the monoalkyltrialkoxysilane is methyltriethoxysilane.
5. The process of claim 4 wherein the monoalkyltrialkoxysilane is present in an amount from 10 to 50 ppm based on the inert hydrocarbon medium.
6. The process of claim 5 wherein the inert hydrocarbon medium is hexane.
7. The process of claim 2 wherein the first and second polymerization reactors are connected in series and the monoalkyltrialkoxysilane is added to the first polymerization reactor and transferred to the second polymerization reactor with ethylene homopolymer produced in said first polymerization reactor.
8. The process of claim 2 wherein the monoalkyltrialkoxysilane is added directly to the second polymerization reactor.