Biodegradable paper-based laminate with oxygen and moisture barrier properties and method for making biodegradable paper-based laminate
Biodegradable laminates including biodegradable polymers have oxygen and moisture barrier properties. The oxygen and moisture barrier layers are biodegradable. If the barrier layers have poor adhesion, degradable tie layers can be included to improve adhesion. Combination of laminate structures can be formed to increase the overall oxygen and moisture barrier characteristics. The biodegradable laminates can be formed by extrusion.
1. A product in the form of a cup comprising a laminate forming moisture barriers, said laminate comprising:
a paperboard substrate having a separate interior product facing surface and a separate exterior surface;
a first moisture protectant layer is coated directly only on said interior surface of said paperboard substrate and comprising at least one biodegradable polyester polymer, wherein the first moisture protectant layer has a coat weight of from 5 to 30 lbs/3000 ft 2 ; and
a second moisture protectant layer is coated directly only on said exterior surface of said paperboard substrate and comprising at least one biodegradable polyester polymer, wherein the second moisture protectant layer has a coat weight of from 5 to 30 lbs/3000 ft 2 and is separate from the first moisture protectant layer coated on and directly adhered to said interior surface of said substrate.
2. The product according to claim 1 , wherein the second moisture protectant layer further comprises from 5 to 20 percent by weight of at least one filler selected from the group consisting of calcium carbonate and starch.
3. The product according to claim 1 , wherein the first moisture protectant layer further comprises from 5 to 20 percent by weight of at least one filler selected from the group consisting of calcium carbonate and starch.
4. The product according to claim 1 , wherein the first moisture protectant layer comprises polylactic acid and from 5 to 20 percent by weight of at least one filler selected from the group consisting of calcium carbonate and starch.
5. The product according to claim 1 , wherein the first moisture protectant layer comprises at least one biodegradable polyester polymer selected from the group consisting of compostable polylactic acid and a compostable polyhydroxyalkanoate.
6. The product according to claim 1 , wherein the second moisture protectant layer comprises at least one biodegradable polyester polymer selected from the group consisting of compostable polylactic acid and a compostable polyhydroxyalkanoate.
7. The product according to claim 6 , wherein the second moisture protectant layer further comprises from 5 to 20 percent by weight of at least one filler.
8. The product according to claim 7 , wherein the second moisture protectant layer comprises from 5 to 20 percent by weight of at least one filler selected from the group consisting of calcium carbonate, starch, clay kaolin, talc, cellulose fibers, and diatomaceous earth.
9. The product according to claim 5 , wherein the first moisture protectant layer further comprises from 5 to 20 percent by weight of at least one filler.
10. The product according to 9 , wherein the first moisture protectant layer comprises from 5 to 20 percent by weight of at least one filler selected from the group consisting of calcium carbonate, starch, clay kaolin, talc, cellulose fibers, and diatomaceous earth.
11. The product according to claim 3 , wherein the first moisture protectant layer comprises from 5 to 20 percent by weight of calcium carbonate as the filler.
12. The product according to claim 4 , wherein the second moisture protectant layer comprises from 5 to 20 percent by weight of calcium carbonate as the filler.