Optimized graphite electrode pin configuration
View Patent ↗A pin for use in connecting graphite electrodes into a joint, where the pin has at least one male tang having a tang factor, defined as the ratio of male tang length to diameter of the electrode into which hit is to be threaded, of at least about 0.60.
1. A pin for use in forming a graphite electrode joint, the pin comprising at least one male tang having a ratio of male tang length to diameter of an electrode into which it is to be threaded of at least 0.60, wherein the diameter of the electrode is at least about 220 mm.
2. The pin of claim 1 , wherein the male tang has a diameter and the ratio of the diameter of the male tang at its base to male tang length is no greater than about 2.5 times the ratio of male tang length to the diameter of the electrode into which it is to be threaded.
3. The pin of claim 2 , wherein the ratio of the diameter of the male tang at its base to male tang length varies with the ratio of male tang length to electrode diameter such that for every 0.01 higher than 0.60 the ratio of male tang length to electrode diameter is, the ratio of the diameter of the male tang at its base to the ratio of male tang length to electrode diameter is about 0.016 lower than 2.5.
4. The pin of claim 1 , wherein the male tang has a taper and further wherein for a pin having a ratio of male tang length to electrode diameter of 0.85 or lower, the ratio of the taper of the male tang to the ratio of male tang length to electrode diameter is at least about 15.
5. The pin of claim 4 , wherein the ratio of the taper of the male tang to the ratio of male tang length to electrode diameter varies with the ratio of male tang length to electrode diameter such that for every 0.01 lower than 0.85 the ratio of male tang length to electrode diameter is, the ratio of the taper of the male tang to the ratio of male tang length to electrode diameter is about 1.25 higher than 15.
6. An electrode joint comprising a pin and two graphite electrodes, wherein each of the two graphite electrodes has a diameter of at least about 220 mm, the pin having a male tang having a ratio of male tang length to diameter of at least one of the electrodes of at least 0.60, and at least one electrode comprising a female threaded socket, wherein the male threaded tang engages the female threaded socket to form the joint.
7. The joint of claim 6 , wherein the male tang has a diameter and the ratio of the diameter of the male tang at its base to male tang length is no greater than about 2.5 times the ratio of male tang length to electrode diameter.
8. The joint of claim 7 , wherein the ratio of the diameter of the male tang at its base to male tang length varies with the ratio of male tang length to electrode diameter such that for every 0.01 higher than 0.60 the ratio of male tang length to electrode diameter is, the ratio of the diameter of the male tang at its base to the ratio of male tang length to electrode diameter is about 0.016 lower than 2.5.
9. The joint of claim 6 , wherein the male tang has a taper and further wherein for a pin having a ratio of male tang length to electrode diameter of 0.85 or lower, the ratio of the taper of the male tang to the ratio of male tang length to electrode diameter is at least about 15.
10. The joint of claim 9 , wherein the ratio of the taper of the male tang to the ratio of male tang length to electrode diameter varies with the ratio of male tang length to electrode diameter such that for every 0.01 lower than 0.85 the ratio of male tang length to electrode diameter is, the ratio of the taper of the male tang to the ratio of male tang length to electrode diameter about 1.25 higher than 15.
11. A process for preparing a pin for use in forming a graphite electrode joint, the process comprising
(a) mixing coke and a pitch binder, to form a stock blend;
(b) extruding the stock blend to form a green stock;
(c) baking the green stock to form a carbonized stock;
(d) graphitizing the carbonized stock by maintaining the carbonized stock at a temperature of at least about 2500° C. to form a graphitized stock;
(e) machining the graphitized stock so as to form a pin having at least one male tang having a ratio of male tang length to diameter of the electrode into which it is to be threaded of at least 0.60, wherein the diameter of the electrode is at least about 220 mm.
12. The process of claim 11 , wherein the male tang has a diameter and the ratio of the diameter of the male tang at its base to male tang length varies with the ratio of male tang length to electrode diameter such that for every 0.01 higher than 0.60 the ratio of male tang length to electrode diameter is, the ratio of the diameter of the male tang at its base to the ratio of male tang length to electrode diameter is about 0.016 lower than 2.5.
13. The process of claim 11 , wherein the male tang has a taper and further wherein for a pin having a ratio of male tang length to electrode diameter of 0.85 or lower, the ratio of the taper of the male tang to the ratio of male tang length to electrode diameter is at least about 15.
14. The process of claim 13 , wherein the ratio of the taper of the male tang to the ratio of male tang length to electrode diameter varies with the ratio of male tang length to electrode diameter such that for every 0.01 lower than 0.85 the ratio of male tang length to electrode diameter is, the ratio of the taper of the male tang to the ratio of male tang length to electrode diameter is about 1.25 higher than 15.