Thin-layer lignocellulose composites having increased resistance to moisture
View Patent ↗A method to produce thin-layer lignocellulosic composites, such as wood-based doorskins, that exhibit substantial resistance to moisture is disclosed. In an embodiment, the method includes the steps of forming a mixture including a refined lignocellulosic fiber, wax, and an organic isocyanate resin. The mixture is initially pressed to form a loose mat. Subsequently, the mat is pressed between two dies at an elevated temperature and pressure to further reduce the thickness of the mat and to promote the interaction of the resin with the lignocellulosic fibers. In an embodiment, a release agent is included as part of the fiber mixture, or sprayed onto the surface of the mat. The thin-layer lignocellulosic composites of the present invention exhibit strong surface strength, high adhesiveness, and a 50% reduction in linear expansion and thickness swelling upon exposure to a high moisture environment as compared to thin-layer composites that do not include the isocyanate resin.
1. A door skin, comprising:
a lignocellulosic composite formed from a mixture comprising:
about 80% to 95% by weight of lignocellulosic fiber, having a moisture content of between 7% and 20% by weight, the lignocellulosic fiber selected from at least one of the following: straw, hemp, sisal, cotton stalk, wheat, bamboo, jute, salt water reed, palm frond, flax, groundnut shell, hard wood, and soft wood;
an organic isocyanate resin;
an internal release agent; and
at least one type of wax,
the door skin having a thickness of between 0.03937 inches (1 mm) and 0.250 inches (6.35 mm) as a result of pressure between two dies at an elevated temperature and pressure and for a sufficient time to allow the isocyanate resin to interact with the lignocellulosic fiber.
2. The door skin of claim 1 , wherein the mixture comprises up to about 2% by weight of wax.
3. The door skin of claim 1 , wherein the release agent comprises an emulsion of surfactants and polymers.
4. The door skin of claim 1 , wherein the release agent is added to the wood mixture prior to pressing the mixture into a thin-layer composite.
5. The thin door skin of claim 4 , wherein the amount of release agent added to the composite ranges from about 0.5% to about 8% by weight.
6. The door skin of claim 1 , wherein the mixture is preformed into a loose mat, and an additional release agent is sprayed onto at least one surface of the mat prior to pressing the mixture into a thin layer composite.
7. The door skin of claim 6 , wherein the amount of release agent sprayed on to the mat surface comprises 0.1 to 8.0 grams solids per square foot (1.1 to 86.1 grams per square meter) of the surface.
8. The door skin of claim 1 , wherein the moisture content of the fiber ranges from about 10% to about 14% moisture by weight.
9. The door skin of claim 1 , wherein the isocyanate comprises diphenylmethane diisocyanate or toluene diisocyanate.
10. The door skin of claim 1 , wherein the isocyanate comprises diphenylmethane-4,4′-diisocyanate.
11. The door skin of claim 1 , wherein the door skin has a resistance to moisture which comprises up to a 50% reduction in linear expansion and thickness swelling after being immersed for 24 hours in 70° F. (21° C.) water than a thin-layer composite comprising a resin that does not include isocyanate.
12. The door skin of claim 1 , wherein said door skin has a resistance to moisture which comprises a thickness swelling of less than 15% after being immersed for 24 hours in water at 70° F. (21° C.).
13. The door skin of claim 1 , wherein the door skin thickness ranges from about 0.110 inches (2.79 mm) to 0.130 inches (3.30 mm).
14. The door skin of claim 1 , wherein the door skin has a density of less than about 60 pounds per cubic foot (962 kg/m 3 ).
15. The door skin of claim 1 , wherein the door skin has a density of less than about 55 pounds per cubic foot (881.2 kg/m 3 ).
16. The door skin of claim 1 , wherein the door skin is suitable for priming or painting despite the inclusion of the release agent.
17. The door skin of claim 1 wherein at least one of the dies is coated with an anti-bonding agent including a ceramic material.
18. The door skin of claim 1 , further comprising a surface area of a standard door face.
19. The door skin of claim 1 , in which the pressure between the two dies is greater than or equal to 1200 psi.
20. The door skin of claim 1 , in which the wax is selected from at least one of the following: paraffin wax, polyethylene wax, polyoxyethylene wax, microcrystalline wax, shellac wax, ozokerite wax, montan wax, emulsified wax, and slack wax.
21. The door skin of claim 1 , in which an external release agent is applied to the mixture.
22. The door skin of claim 1 , further comprising:
an outer surface intended to be on the outside of a door, the outer surface including a recessed portion; and
an inner surface opposing the outer surface, the inner surface including a protruding portion that is the mirror image of the recessed portion of the outer surface.
23. The door skin of claim 1 , further comprising:
an outer surface intended to be on the outside of a door, the outer surface including a grain texture or grain-like pattern.
24. The door skin of claim 1 , wherein the door skin has a surface area of 20 square feet or more.
25. The door skin of claim 1 , wherein the door skin has a thickness greater than 0.100 inches.
26. A door skin, comprising:
a lignocellulosic composite formed from a mixture of about 80% to 95% by weight of at least one type of lignocellulosic fiber, wherein the fiber has a moisture content of between 7% and 20% by weight;
at least 5% by weight of an organic isocyanate resin;
an internal release agent;
at least one type of wax, the door skin having a thickness of between 0.03937 inches (1 mm) and 0.250 inches (6.35 mm) as a result of pressure between two dies at an elevated temperature and pressure and for a sufficient time to allow the isocyanate resin to interact with the lignocellulosic fiber.
27. The door skin of claim 26 , wherein the door skin has a density of less than about 60 pounds per cubic foot (962 kg/m 3 ).
28. The door skin of claim 26 wherein at least one of the dies is coated with an anti-bonding agent that includes a ceramic material.
29. The door skin of claim 26 , further comprising a surface area of a standard door face.
30. The door skin of claim 26 , further comprising:
an outer surface intended to be on the outside of a door, the outer surface including a grain texture or grain-like pattern.
31. The door skin of claim 26 , further comprising:
an outer surface and an opposing inner surface, the outer surface including a recessed portion and the inner surface including a protruding portion that is the mirror image of the recessed portion.
32. The door skin of claim 26 , wherein the door skin has a surface area of 20 square feet or more.
33. The door skin of claim 26 , wherein the door skin has a thickness greater than 0.100 inches.
34. A door skin, comprising;
a lignocellulosic composite mixture including:
about 80% to 95% by weight of lignocellulosic fiber;
an organic isocyanate resin;
an internal release agent; and
at least one type of wax,
the door skin having a thickness of between 0.03937 inches (1 mm) and 0.250 inches (6.35 mm) as a result of pressure between two dies at an elevated temperature and pressure and for a sufficient time to allow the isocyanate resin to interact with the lignocellulosic fiber, the door skin having an outer surface and an opposing inner surface, the outer surface intended to be on the outside of a door, the outer surface including a recessed portion and the inner surface including a protruding portion that is the mirror image of the recessed portion.
35. The door skin of claim 34 , wherein at least one of the dies is treated with an anti-bonding agent.
36. The door skin of claim 34 , wherein the mixture includes at least 5% by weight of the organic isocyanate resin.
37. A door skin, comprising;
a lignocellulosic composite mixture including:
about 80% to 95% by weight of lignocellulosic fiber;
an organic isocyanate resin;
an internal release agent; and
at least one type of wax,
the door skin having a thickness of between 0.03937 inches (1 mm) and 0.250 inches (6.35 mm) as a result of pressure between two dies at an elevated temperature and pressure and for a sufficient time to allow the isocyanate resin to interact with the lignocellulosic fiber, the door skin having an impression in an outer surface with a grain texture or grain-like pattern.
38. The door skin of claim 37 , wherein at least one of the dies is treated with an anti-bonding agent.
39. The door skin of claim 37 , wherein the mixture includes at least 5% by weight of the organic isocyanate resin.