Welding light metal workpieces by reaction metallurgy
View Patent ↗Aluminum alloy workpieces and/or magnesium alloy workpieces are joined in a solid state weld by use of a reactive material placed, in a suitable form, at the joining surfaces. Joining surfaces of the workpieces are pressed against the interposed reactive material and heated. The reactive material alloys or reacts with the workpiece surfaces consuming some of the surface material in forming a reaction product comprising a low melting liquid that removes oxide films and other surface impediments to a welded bond across the interface. Further pressure is applied to expel the reaction product and to join the workpiece surfaces in a solid state weld bond.
1. A method of forming a solid-state weld between a first joining surface of a first light metal alloy workpiece, the light metal being aluminum or magnesium, and a second joining surface of a second light metal alloy workpiece; the method comprising:
selecting, as a reactive material, a metallic element, or an alloy of two or more elements, or a mixture of two or more different elements or alloys, in a form to be placed between and in contact with the first joining surface and the second joining surface, the reactive material being selected to react with at least the first light metal alloy joining surface upon being heated to a temperature below the solidus temperature of the first light metal alloy to form a reaction product comprising a liquid comprising the reactive material and the light metal alloy element, and cavities are provided in one of the joining surfaces to hold the reactive material; the following steps being conducted at ambient conditions,
preparing an assembly of the workpieces with their respective joining surfaces face-to-face and with at least one of the joining surfaces in contact with the reactive material, the amount of reactive material being predetermined to consume a specified amount of one or both workpieces in forming the reaction product;
pressing the assembly at a first pressure level so that the facing surfaces engage the reactive material, and heating the reactive material for a predetermined time to form the reaction product and consume portions of the facing workpieces, including consumption of surface alloy material defining the cavities;
increasing the pressure on the assembly to a higher pressure level to force substantially all formed reaction product from between the residual joining surfaces while limiting the displacement of the joining surfaces to a predetermined value; and, thereafter
holding the joining surfaces against each other until a solid-state welded joint is formed substantially coextensively with the intended joining surfaces.
2. A method of making a solid-state weld as recited in claim 1 in which a first aluminum alloy workpiece is joined to a second aluminum alloy workpiece and a plurality of cavities are provided in one of the joining surfaces to hold the reactive material and the reactive material comprises at least one metal element selected from the group consisting of copper, magnesium, silicon, and zinc.
3. A method of making a solid-state weld as recited in claim 1 in which a first magnesium alloy work piece is joined to a second magnesium alloy workpiece and a plurality of cavities are provided in one of the joining surfaces to hold the reactive material and the reactive material comprises at least one metal element selected from the group consisting of copper, magnesium, silicon, and zinc.
4. A method of making a solid-state weld as recited in claim 1 in which both workpieces are light metal alloy sheets having a thickness in the range about three-quarters of a millimeter to about four millimeters and the amount of reactive material is predetermined to consume no more than about ten percent of the thickness of the thinner of the two sheet workpieces.
5. A method of making a solid-state weld as recited in claim 4 in which the workpieces are aluminum alloy sheets and the reactive material comprises copper.
6. A method of making a solid-state weld as recited in claim 1 in which the first light metal alloy workpiece is formed by casting the first light metal alloy and the joining surface of the cast first light metal alloy workpiece is thereby initially formed with cast-in-place cavities for holding the reactive material, the reactive material, when heated, reacting with joining surface alloy material defining the cavities in forming the reaction product.
7. A method of making a solid-state weld as recited in claim 1 further comprising:
forming cavities for reactive material in the joining surface of at least one of the workpieces and placing reactive material in the cavities and on the joining surface around the cavities, and
preparing an assembly of the workpieces so that the reactive material, when heated, reacts with joining surface alloy material defining the cavities in forming the reaction product, the combination of the applied pressure and the reaction of the reactive material acting to level the workpiece surface for the solid-state welded joint.
8. The method of claim 1 wherein the first predetermined period of time is established as the time necessary for the reaction product to remove metal oxides from the facing workpiece surfaces.
9. The method of claim 1 where the assembly is pressed and heated using a welding servo gun.
10. The method of claim 1 where the assembled workpieces are heated by at least one of resistance heating, conductive heating and induction heating.
11. The method of claim 1 where the assembled workpieces are subjected to mechanical motion, mechanical vibration, or ultrasonic excitation transverse to the joining surfaces to promote formation of the reaction product.