SEED CRYSTAL COATING FOR GYPSUM WALLBOARD FACING
Facing material useful in the manufacture of gypsum wallboard is surfaced treated in order to adhere an amount of seed crystals to improve the adhering affinity of the facing material for wet plaster thereby permitting the manufacture of gypsum wallboard with little or no added starch and reduced amounts of water. Various means for adhering the seed crystals to the facing material are described as well as, a method of converting the facing material and wallboards containing the facing material are also described.
1 . A treated facing material for use in gypsum wallboards comprising:
a facing material wherein a surface of the facing material is treated with an amount of a seed crystal adhered to the surface of the facing material wherein the seed crystal is selected from the group consisting of CaCO 3 , CaSO 4 , BaSO 4 , Na 2 SO 4 , KAl(SO 4 ) 2 , CaMg(CO 3 ) 2 , MgCO 3 , K 2 SO 4 , Fe[SO 4 ] 3 /FeSO 4 , Al 2 [SO 4 ] 3 , and their hydrate forms.
2 . The treated facing material for use in gypsum wallboards of claim 1 wherein the seed crystal comprises CaSO 4 and its hydrate forms.
3 . The treated facing material for use in gypsum wallboards of claim 2 wherein the CaSO 4 is in its anhydrite form.
4 . The treated facing material for use in gypsum wallboards of claim 2 wherein the CaSO 4 is in its hemihydrate form.
5 . The treated facing material for use in gypsum wallboards of claim 2 wherein the CaSO 4 is in its dihydrate form.
6 . The treated facing material for use in gypsum wallboards of claim 1 wherein the facing material is selected from the group consisting of papers, glass fiber sheets and synthetic sheet materials.
7 . The treated facing material for use in gypsum wallboards of claim 6 wherein the synthetic sheet materials may be selected from the group consisting of polyethylene, polypropylene, polyvinylchloride, polyurethane and epoxy.
8 . A process for producing a treated facing material for use in gypsum wallboards comprising the steps of:
a) obtaining a facing material;
b) obtaining an amount of a seed crystal; and
c) adhering the seed crystal to at least one surface of the facing material to obtain a surface of the facing material with a seed crystal coating, wherein the seed crystal is selected from the group consisting of CaCO 3 , CaSO 4 , BaSO 4 , Na 2 SO 4 , KAl(SO 4 ) 2 , CaMg(CO 3 ) 2 , MgCO 3 , K 2 SO 4 , Fe[SO 4 ] 3 /FeSO 4 , Al 2 [SO 4 ] 3 , and their hydrate forms.
9 . The process for producing the treated facing material for use in gypsum wallboards of claim 8 wherein the adhering of the seed crystal is accomplished through the steps of:
i obtaining an amount of an adhering agent;
ii applying the adhering agent to the at least one surface of the facing material; and
iii subsequently applying the seed crystal to the at least one surface of the facing material to obtain the surface of the facing material with the seed crystal coating.
10 . The process for producing the treated facing material for use in gypsum wallboards of claim 9 wherein the adhering agent is water.
11 . The process for producing the treated facing material for use in gypsum wallboards of claim 9 wherein the adhering agent is an adhesive.
12 . The process for producing the treated facing material for use in gypsum wallboards of claim 11 wherein the adhesive is selected from the group consisting of solvent-based, aqueous-based or solventless adhesives.
13 . The process for producing the treated facing material for use in gypsum wallboards of claim 12 wherein the adhesive comprises a latex adhesive.
14 . The process for producing the treated facing material for use in gypsum wallboards of claim 13 wherein the latex adhesive is in the form of a redispersible powder.
15 . The process for producing the treated facing material for use in gypsum wallboards of claim 8 wherein the adhering agent is applied to the at least one surface of the facing material by an application means selected from the group consisting of a doctor blade, a roll, a puddle applicator, a size press, a curtain coater, a water box, and a spray applicator.
16 . The process for producing the treated facing material for use in gypsum wallboards of claim 8 wherein the adhering of the seed crystal is accomplished through the steps of:
i obtaining a facing material capable of absorbing water;
ii applying an amount of water as the adhering agent to the at least one surface of the facing material; and
iii subsequently applying the seed crystal to the at least one surface of the facing material to obtain the surface of the facing material with the seed crystal coating.
17 . The process for producing the treat facing material for use in gypsum wallboards of claim 8 , further comprising using paper as the facing material for use in gypsum wallboards wherein the adhering of the seed crystal is accomplished during a paper production process through applying the seed crystal to a wet surface of the paper during the paper production process to obtain the surface of the facing material with the seed crystal coating.
18 . The process for producing a treated facing material for use in gypsum wallboards of claim 8 wherein the adhering of the seed crystal is accomplished through the steps of:
i obtaining a facing material capable of absorbing water;
ii producing a slurry or solution comprising an amount of water and an amount of seed crystal;
iii applying the slurry comprising water and seed crystal to the at least one surface of the facing material to obtain the surface of the facing material with the seed crystal coating.
19 . A wallboard comprising:
an interior gypsum plaster core; and
a treated facing material comprising:
a facing material wherein a surface of the facing material is treated with an amount of a seed crystal bonded to the surface of the facing material wherein the seed crystal is selected from the group consisting of CaCO 3 , CaSO 4 , BaSO 4 , Na 2 SO 4 , KAl(SO 4 ) 2 , CaMg(CO 3 ) 2 , MgCO 3 , K 2 SO 4 , Fe[SO 4 ] 3 /FeSO 4 , Al 2 [SO 4 ] 3 , and their hydrate forms.