Thermoformed articles made from reactive extrusion products of biobased materials
View Patent ↗The present invention is directed to a method of producing a thermoformable composite by crosslinking PHA and PLA together in the presence of an additive to produce PHA and PLA blend and resins having: (a) a T s value of up to about 180° C.; and (b) a heat distortion index of up to about 160° C. The thermoformable composite is used to make a food or beverage cup, lid, cutlery item, foodservice item, molded tray, or food storage container. The thermoformable composite comprises from about 5% to about 95% by weight of polylactic acid (PLA), from about 5% to about 95% by weight polyhydroxyalkanoate (PHA) polymer, and from about 0.01% to about 60% additives wherein the PLA and PHAs being crosslink together by intermolecular means to enhance performance and processability.
1. A cup lid made of a thermoformable composite, the thermoformable composite comprising from about 5% to about 95% by weight of polylactic acid (PLA), from about 5% to about 95% by weight polyhydroxyalkanoate (PHA) polymer, and from about 0.01% to about 60% additives, the polylactic acid (PLA) has an average molecular weight in the range of from about 15,000 and about 300,000 and wherein the PLA and PHAs being crosslink together by intermolecular means to enhance performance and processability.
2. The cup lid of claim 1 wherein the polyhydroxyalkanoate (PHA) polymer comprises one or more of poly-beta-hydroxybutyrate, poly-alpha-hydroxybutyrate, poly-3-hydroxypropionate, poly-3-hydroxyvalerate, poly-4-hydroxybutyrate, poly-4-hydroxyvalerate, poly-5-hydroxyvalerate, poly-3-hydroxyhexanoate, poly-4-hydroxyhexanoate, poly-6-hydroxyhexanoate, polyhydroxybutyrate-valerate, polyglycolic acid, or polylactic acid.
3. The cup lid of claim 1 wherein the PLA is defined as all stereoisomeric forms of PLA including L- or D-lactides, and racemic mixtures comprising L- and D-lactides, D-polylactic acid, L-polylactic acid (PLLA), D,L-polylactic acid, meso-polylactic acid, and any combination of D-polylactic acid, L-polylactic acid, D,L-polylactic acid and meso-polylactic acid.
4. The cup lid of claim 1 wherein the intermolecular means is tie molecules.
5. The cup lid of claim 1 wherein the intermolecular means is chemical bounding.
6. The cup lid of claim 1 wherein the intermolecular means is combination of tie molecules and chemical bounding.
7. The cup lid of claim 1 the thermoformable composite has a T s value up to about 180° C.
8. The cup lid of claim 1 wherein the thermoformable composite has a T s value in the range of from about 80° C. to about 170° C.
9. The cup lid of claim 1 wherein the thermoformable composite has a heat distortion index of up to about 160° C.
10. The cup lid of claim 1 wherein the thermoformable composite has a heat distortion index of greater than about 60° C.
11. The cup lid of claim 1 wherein the thermoformable composite has a T m in the range of from about 90° to about 200° C.
12. The cup lid of claim 1 wherein thermoformable composite has a T s value greater than about 60° C. and a heat distortion index greater than about 50° C.
13. The cup lid of claim 1 wherein the thermoformable composite comprising from about 20% to about 80% by weight of polylactic acid (PLA), from about 20% to about 80% by weight polyhydroxyalkanoate (PHA) polymer, and from about 0.01% to about 40% additives wherein the PLA and PHAs being crosslink together by intermolecular means.
14. The cup lid of claim 1 wherein the thermoformable composite comprising from about 30% to about 60% by weight of polylactic acid (PLA), from about 30% to about 60% by weight polyhydroxyalkanoate (PHA) polymer, and from about 0.1% to about 35% additives wherein the PLA and PHAs being crosslink together by intermolecular means.