Coating composition with accelerated low temperature cure
A coating composition including an unsaturated resin selected from polyesters, alkyds or combinations thereof; an alkoxy (meth)acrylic functional monomer, and a thermoplastic compound containing active hydrogen groups; a curing agent; and a curing promoter such as at least one metal drier.
1. A method of making a coating composition, comprising reacting the following components to form a coating composition:
(1) a first component A, comprising:
about 20 wt % to about 90 wt %, based on the total weight of the composition, of an unsaturated polyester resin, wherein the unsaturated polyester comprises allyl ether functionality,
about 1 wt % to about 50 wt % of:
an alkoxy (meth)acrylic functional monomer, wherein the functional monomer is selected from di and tri(meth)acrylic functional compounds with about 8 to about 16 ethoxy or propoxy groups along a backbone and
a thermoplastic compound containing active hydrogen groups, wherein the thermoplastic compound is selected from cellulose resins and cellulose derivatized resins; and
about 0.1 wt % to about 3 wt % of least one metal drier, wherein the metal drier is a metal salt of an organic acid, and wherein the metal comprises Co, Mn, Pb, Ce, Zr, Ca, Zn, Bi, Cu, Cr, Li, K, Ni, Mg and mixtures and combinations thereof, and
(2) a second component B, comprising about 0.5 wt % to about 5 wt % of at least one organic peroxide;
wherein the coating composition is substantially free of any of formaldehyde, isocyanate and styrene.
2. The method of claim 1 , wherein component A further comprises about 5 wt % to about 80 wt % of at least one organic solvent.
3. The method of claim 1 , wherein component A further comprises up to about 50 wt % of at least one second (meth)acrylic functional monomer.
4. The method of claim 1 , wherein the metal comprises K, Co, Mg and mixtures and combinations thereof.
5. The method of claim 1 , wherein the metal driers comprise Co.
6. The method of claim 1 , wherein the coating composition further comprises about 0.2 wt % to about 20 wt % of the thermoplastic compound.
7. The method of claim 1 , wherein the thermoplastic compound is selected from cellulose acetate butyrate (CAB), cellulose acetate (CA) and combinations thereof.
8. The method of claim 1 , wherein the thermoplastic compound is cellulose acetate butyrate (CAB).
9. The method of claim 1 , wherein the coating composition further comprises about 0.1 wt % to about 3 wt % of at least one surface active agent.
10. A method, comprising:
(1) providing a coating composition comprising:
an unsaturated polyester resin comprising allyl ether functionality,
an alkoxy (meth)acrylic functional monomer, wherein the functional monomer is selected from di and tri(meth)acrylic functional compounds with about 8 to about 16 ethoxy or propoxy groups along a backbone, and
a thermoplastic compound containing active hydrogen groups reactive under free radical initiated curing, wherein the thermoplastic compound is selected from cellulose acetate butyrate (CAB), cellulose acetate (CA) and combinations thereof;
at least one metal drier, wherein the metal drier is a metal salt of an organic acid, and
a peroxide,
wherein the coating composition is substantially free of any of formaldehyde, isocyanate and styrene; and
(2) applying the coating composition to a substrate.
11. The method of claim 10 , further comprising curing the coating composition to form a cured coating.
12. The method of claim 11 , wherein the coating composition is cured at room temperature for less than about 24 hours.
13. The method of claim 11 , wherein the coating composition is cured at a temperature of about 30° C. to about 60° C. for about 30 minutes to about 60 minutes.
14. The method of claim 11 , wherein the coating composition is cured at a temperature of about 50° C. to about 60° C. for less than about 20 minutes.
15. The method of claim 10 , wherein the coating composition is applied by spraying.
16. The method of claim 14 , wherein the coating composition is applied by spraying with a two component gun system.
17. A substrate having applied thereon a cured coating composition, wherein the coating composition comprises
an unsaturated polyester resin comprising allyl ether functionality;
an alkoxy (meth)acrylic functional monomer, wherein the functional monomer is selected from di and tri(meth)acrylic functional compounds with about 8 to about 16 ethoxy or propoxy groups along a backbone, and
a thermoplastic compound containing active hydrogen groups reactive under free radical initiated curing, wherein the thermoplastic compound is selected from cellulose acetate butyrate (CAB), cellulose acetate (CA) and combinations thereof;
at least one metal drier, wherein the metal drier is a metal salt of an organic acid; and
a peroxide; wherein the coating composition is substantially free of any of formaldehyde, isocyanate and styrene.