WATERBORNE COATING COMPOSITION CONTAINING POLYTRIMETHYLENE ETHER DIOL
The present invention is directed to an aqueous coating composition comprising a polymer having one or more crosslinkable functional groups; a polytrimethylene ether diol from renewable resource having a Mn (number average molecular weight) in a range of from 500 to 10,000; and a crosslinking agent. The aqueous coating composition comprises in a range of from 10% to 80% of water.
1 . An aqueous coating composition comprising:
A) a polymer dissolved or dispersed in water, said polymer comprises one or more crosslinkable functional groups;
B) a polytrimethylene ether diol having a Mn (number average molecular weight) in a range of from 500 to 10,000; and
C) a crosslinking agent having one or more crosslinking functional groups;
wherein said aqueous coating composition comprises in a range of from 10% to 80% of water, percentage based on total weight of the aqueous coating composition.
2 . The aqueous coating composition of claim 1 , wherein said polymer comprises one or more hydroxyl functional groups as the crosslinkable functional groups.
3 . The aqueous coating composition of claim 2 , wherein said polymer is a hydroxyl (meth)acrylic polymer, a hydroxyl polyester, a latex, or a combination thereof.
4 . The aqueous coating composition of claim 3 , wherein said hydroxyl polyester is selected from: one or more linear polyesters having hydroxyl functional groups; one or more branched copolyesters having hydroxyl functional groups; or a combination thereof.
5 . The aqueous coating composition of claim 1 , wherein the crosslinking agent comprises one or more organic polyisocyanates.
6 . The aqueous coating composition of claim 5 , wherein said one or more organic polyisocyanates are selected from the group consisting of aliphatic polyisocyanates, cycloaliphatic polyisocyanates, aromatic polyisocyanates, tri-functional isocyanates and isocyanate adducts.
7 . The aqueous coating composition of claim 1 , wherein the polytrimethylene ether diol has a Mn in a range of from 500 to 4,000, a Tg of about −75° C. and a hydroxyl number in a range of from 20 to 200.
8 . The aqueous coating composition of claim 7 , wherein the polytrimethylene ether dial is a blend of high and low molecular weight polytrimethylene ether dials wherein the high molecular weight polytrimethylene ether dial has an Mn in a range of from 1,000 to 4,000 and the low molecular weight polytrimethylene ether dial has an Mn in a range of from 150 to 500 and the average Mn of the blend is in a range of from 500 to 4,000.
9 . The aqueous coating composition of claim 1 , wherein the polytrimethylene ether diol is polymerized from bio-derived 1,3-propanediol.
10 . The aqueous coating composition of claim 1 further comprising pigments, ultraviolet light stabilizers, ultraviolet light absorbers, antioxidants, hindered amine light stabilizers, leveling agents, rheological agents, thickeners, antifoaming agents, wetting agents, catalysts, or a combination thereof.
11 . The aqueous coating composition of claim 1 , wherein said aqueous coating composition is formulated as a 2K refinish coating composition.
12 . An article coated with the aqueous coating composition of claim 1 .
13 . The article of claim 12 , wherein said article is an automotive body or an automotive body part.
14 . A process for coating a substrate to form a coating layer thereon, said process comprising the steps of;
a) providing an aqueous coating composition comprising:
A) a polymer dissolved or dispersed in water, said polymer comprises one or more crosslinkable functional groups;
B) a polytrimethylene ether diol having a Mn (number average molecular weight) in a range of from 500 to 10,000; and
C) a crosslinking agent having one or more crosslinking functional groups;
wherein said aqueous coating composition comprises in a range of from 10% to 80% of water, percentage based on total weight of the aqueous coating composition;
b) applying said aqueous coating composition over the substrate to form a layer of said aqueous coating composition thereon; and
c) curing said layer of the aqueous coating composition to form said coating layer.
15 . The process of claim 14 , wherein said polymer comprises one or more hydroxyl functional groups as the crosslinkable functional groups.
16 . The process of claim 15 , wherein said polymer is a hydroxyl acrylic polymer, a hydroxyl polyester, a latex, or a combination thereof.
17 . The process of claim 16 , wherein said hydroxyl polyester is selected from: one or more linear polyesters having hydroxyl functional groups; one or more branched copolyesters having hydroxyl functional groups; or a combination thereof.
18 . The process of claim 14 , wherein the crosslinking agent comprises one or more organic polyisocyanates.
19 . The process of claim 18 , wherein said one or more organic polyisocyanates are selected from the group consisting of aliphatic polyisocyanates, cycloaliphatic polyisocyanates, aromatic polyisocyanates, tri-functional isocyanates and isocyanate adducts.
20 . The process of claim 14 , wherein said aqueous coating composition further comprises pigments, ultraviolet light stabilizers, ultraviolet light absorbers, antioxidants, hindered amine light stabilizers, leveling agents, rheological agents, thickeners, antifoaming agents, wetting agents, catalysts, or a combination thereof.
21 . The process of claim 14 , wherein said aqueous coating composition is formulated as a 2K refinish coating composition.
22 . The process of claim 14 , wherein said substrate is an automotive body or an automotive body part.
23 . An article coated with the process of claim 14 .
24 . The article of claim 23 , wherein said article is an automotive body or an automotive body part.