Use of composite of lightweight hollow core having adhered or embedded cement in cementing a well
View Patent ↗A lightweight composite having an activated surface contains a lightweight hollow core particle having cement grains which may be adhered to the hollow core or embedded in the surface of the hollow core. The hollow core particle may be prepared from calcium carbonate and a mixture of clay, such as bentonite, and a glassy inorganic material, such as glass spheres, glass beads, glass bubbles, borosilicate glass and fiberglass.
1. A method of cementing within a gas or oil well comprising:
(a) pumping into the well a cementitious slurry containing a composite, wherein the composite comprises a lightweight hollow core and cement grains, wherein the lightweight hollow core is formed from calcium carbonate, clay and an inorganic material and wherein the cement grains are adhered to the surface of the lightweight hollow core, embedded in the surface of the lightweight hollow core or are both adhered to the surface of the lightweight hollow core and embedded in the surface of the lightweight hollow core and further wherein the composite is prepared by adding cement powder to the lightweight hollow core, drying the mixture, heat treating the mixture at a rate of 10° C./min to 800° C., and then cooling the resulting product; and
(b) allowing the slurry to harden to a solid mass.
2. The method of claim 1 , wherein the particle size of the lightweight hollow core is between from about 20 to about 40 mesh.
3. The method of claim 1 , wherein at least a portion of the surface of the lightweight hollow core is treated with a coating layer and further wherein the cement grains are adhered onto the coating layer.
4. The method of claim 1 , wherein the inorganic material is spherical.
5. The method of claim 1 , wherein the lightweight hollow core is formed from bentonite and an inorganic material selected from the group consisting of inorganic glass, pozzolanic microspheres and ceramic spheres.
6. The method of claim 5 , wherein the inorganic glass is selected from the group consisting of glass spheres, glass beads, glass bubbles, borosilicate glass and fiberglass.
7. The method of claim 6 , wherein the inorganic glass is borosilicate glass.
8. The method of claim 7 , wherein the lightweight hollow core is formed from about 5 to about 50 percent by weight bentonite and from about 50 to about 95 percent by weight borosilicate glass.
9. The method of claim 1 , wherein the composite is prepared by treating at least a portion of the lightweight hollow core with a coating layer, applying dry cement onto the coating layer, and hardening the cement.
10. The method of claim 1 , wherein the cement grains are adhered to the surface of the lightweight hollow core.
11. The method of claim 1 , wherein the cement grains are embedded in the surface of the lightweight hollow core.
12. The method of claim 1 , wherein the cement grains are both adhered to the surface of the lightweight hollow core and embedded in the surface of the lightweight hollow core.
13. The method of claim 1 , wherein the clay is bentonite.
14. The method of claim 1 , wherein the particle size of the lightweight hollow core is from about 10 micrometers to about 1,000 micrometers.
15. The method of claim 1 , wherein the density of the lightweight hollow core is between from about 0.6 g/cc to about 1.1 g/cc.
16. The method of claim 1 , wherein the cement grains are grains of Portland cement.
17. A method of cementing a casing within a wellbore comprising:
(a) pumping into the wellbore a cementitious slurry containing a composite, wherein the composite comprises a lightweight hollow core and Portland cement grains, wherein the lightweight hollow core is formed from calcium carbonate, clay and an inorganic material and wherein the Portland cement grains are adhered to the surface of the lightweight hollow core, embedded in the surface of the lightweight hollow core or are both adhered to the surface of the lightweight hollow core and embedded in the surface of the lightweight hollow core and further wherein the composite is prepared by adding cement powder to the lightweight hollow core, drying the mixture, heat treating the mixture at a rate of 10° C./min to 800° C., and then cooling the resulting product; and
(b) allowing the slurry to harden to a solid mass.
18. The method of claim 17 , wherein the clay is a bentonite.
19. The method of claim 17 , wherein the inorganic material is spherical.
20. A method of cementing within a gas or oil well comprising:
(a) pumping into the well a cementitious slurry containing a composite wherein:
(i) the cementitious slurry has a density ranging from about 13.0 pounds per gallon (ppg) to about 6.0 ppg;
(ii) the composite comprises a lightweight hollow core and cement grains, wherein the lightweight hollow core is formed from calcium carbonate, clay and an inorganic material selected from the group consisting of glass spheres, glass beads, glass bubbles, borosilicate glass and fiberglass;
(iii) the cement grains are adhered to the surface of the lightweight hollow core, embedded in the surface of the lightweight hollow core or are both adhered to the surface of the lightweight hollow core and embedded in the surface of the lightweight hollow core; and
(iv) wherein the composite is prepared by adding cement powder to the lightweight hollow core, drying the mixture, heat treating the mixture at a rate of 10° C./min to 800° C., and then cooling the resulting product; and
(b) allowing the slurry to harden to a solid mass.
21. The method of claim 20 , wherein the cement grains are grains of Portland cement.