POWDER COATING COMPOSITION FOR THERMOPLASTIC COMPOSITES
The present invention provides a method for coating a thermoplastic composite comprising the steps of: i) providing a thermoplastic powder coating composition comprising one or more functionalized polyolefins selected from the group consisting of functionalized polyethylenes, functionalized polypropylenes, ethylene acid copolymers, ionomer resins, functionalized ethylene vinyl acetate (EVA) copolymers and functionalized ethylene alkyl(meth)acrylate copolymers, and ii) applying the thermoplastic powder coating composition to the thermoplastic composite to form a powder coating on the thermoplastic composite. The method according to the invention provides a strong adhesion of the thermoplastic powder coating onto the thermoplastic composite, a high scratch and scuff resistance as well as a surface appearance of a high quality finish and outdoor performance.
1 . A method for coating a thermoplastic composite comprising the steps of:
i) providing a thermoplastic powder coating composition comprising one or more functionalized polyolefins selected from the group consisting of functionalized polyethylenes, functionalized polypropylenes, ethylene acid copolymers, functionalized ethylene vinyl acetate (EVA) copolymers and functionalized ethylene alkyl(meth)acrylate copolymers, and
ii) applying the thermoplastic powder coating composition to the thermoplastic composite to form a powder coating on the thermoplastic composite.
2 . The method according to claim 1 , wherein the thermoplastic composite is made from a mixture of a thermoplastic material and glass fiber material in a ratio of 60:40 to 10:90.
3 . The method according to claim 2 , wherein the thermoplastic material is polypropylene.
4 . The method according to claim 1 , wherein the one or more functionalized polyolefins of the thermoplastic powder coating composition are colored.
5 . The method according to claim 1 , wherein the functionalized polyolefin of the powder coating composition has a melt flow index less than 300 g/10 min according to ASTM Method No. D1238 at 190° C. using a 2160 g weight.
6 . The method according to claim 1 , wherein the powder coating composition has a particle size (D90 value) less than or equal to 800 μm according to ISO 3310-1 done on a Malvern Mastersizer 2000.
7 . The method according to claim 1 , wherein the functionalized polyolefin of the powder coating composition comprises one or more ionomer resins.
8 . The method according to claim 1 , further comprising the step of adding at least one additional coating layer comprising one or more ethylene copolymers and/or ionomer resins.
9 . The method according to claim 8 , wherein the at least one additional coating layer is a clear coat layer.
10 . An article comprising a thermoplastic composite coated with the process according claim to 1 .
11 . The article according to claim 10 , wherein the article is an article for use in vehicular applications, a construction article or an advertising article.