Nanocrystallinecellulose (NCC) in tape joint compound (JC)
View Patent ↗A joint compound with improved crack resistance is formed by combining water, a filler such as calcium carbonate, a latex emulsion binder, a thickening system such as methylhydroxyethyl cellulose, and nanocrystalline cellulose. The nanocrystalline cellulose is provided in an amount effective to reduce the crack formation during drying.
1. A joint compound comprising nanocrystalline cellulose, water, a filler, a binder and a thickener, wherein the amount of the nanocrystalline cellulose is effective to improve crack resistance of the joint compound upon drying; wherein the nanocrystalline cellulose has a length to diameter ratio of from about 20 to 200; and wherein the diameter of the nanocellulose is less than 60 nanometers.
2. The joint compound of claim 1 , wherein the nanocrystalline cellulose is present in an amount of from about 0.05 to about 0.5 percent by weight based on the total weight of the compound.
3. The joint compound of claim 1 , wherein the filler is selected from the group consisting of calcium carbonate, calcium sulfate dihydrate, limestone, calcium sulfate hemihydrate, and combinations thereof.
4. The joint compound of claim 3 , wherein the filler comprises calcium carbonate.
5. The joint compound of claim 4 , wherein the filler is present in an amount of from about 45 to about 65 percent by weight based on the total weight of the compound.
6. The joint compound of claim 1 , wherein the binder is selected from the group consisting of polyvinyl alcohol, ethylene vinyl acetate latex, polyvinyl acetate) latex, starch, casein, polyacrylamide, copolymers of acrylamide and acrylic acid, and combinations thereof.
7. The joint compound of claim 6 , wherein the binder is present in an amount of from about 1 to about 2.5 percent by weight based on the total weight of the compound.
8. The joint compound of claim 1 , wherein the thickener is selected from the group consisting of carboxymethyl cellulose, ethylhydroxyethyl cellulose, hydroxyethyl cellulose, hydrophobically modified hydroxyethyl cellulose, hydroxypropylmethyl cellulose, methylhydroxyethyl cellulose, methylcarboxycellulose, hydroxypropyl guar, underivatized guar, and combinations thereof.
9. The joint compound of claim 8 , wherein the thickener is present in an amount of from about 0.3 to about 0.5 percent by weight based on the total weight of the compound.
10. The joint compound of claim 8 , wherein the thickener is methylhydroxyethyl cellulose.
11. The joint compound of claim 1 further comprising petlite.
12. The joint compound of claim 1 further comprising a biocide.
13. The joint compound of claim 12 , wherein the biocide is present in an amount ranging from about 0.05 to about 1.0% by weight based on the total weight of the compound.
14. The joint compound of claim 1 further comprising about 1.5 to about 3.5 percent by weight of clay based on the total weight of the compound.
15. The joint compound of claim 14 , wherein the clay comprises attapulgite clay.
16. The joint compound of claim 1 further comprising mica.
17. The joint compound of claim 1 , wherein the nanocrystalline cellulose is present in an amount of about 0.05 to about 0.1% by weight and the thickener is present in an amount of from about 0.3 to 0.5% by weight based on the total weight of the compound.